Chung-yun Hse

Abstraet Wettabillty of southern pine veneers was judged by measuring the contact angles made by 36 phenol formaldehyde resins. Formulation of the resins was by factorial design. the molar ratios of sodium hydroxide to phenol being 0.4, 0.7, and 1.0, the levels of resin solids content in the reaction mixture 37, 40, and 43 percent, and the molar ratios of formaldehyde to phenol 1.6, 1.9, 2.2, and 2.5. As molar ratios of sodium hydroxide to phenol increased and ratios of formaldehyde to phenol decreased. the contact angle decreased. Contact angle was not correlated with solids content. Contact angle on earlywood was less than that on latewood, apparently because earlywood surfaces were rougher. Contact angle was positively correlated with glue bond quality as tested by wet shear strength, percent of wood failure, and percent of delamination. High contact angle of the resln-and low wetting of the veneermay prevent excess glue penetration, which often causes poor bonds In southern pine plywood. resins having a wide range of physico-chemical properties. It discusses the effects of resin formulation on ~'ettability as measured by contact angles as well as the relation betw~ contact angle and bond quality.