Behaviour of Natural and Implanted Iron during Annealing of Multicrystalline Silicon Wafers
نویسندگان
چکیده
Changes in the concentration of interstitial iron in multicrystalline silicon wafers after high temperature annealing (900oC) have been monitored by carrier lifetime measurements. Two cooling rates were investigated. The first was considered ‘fast’, meaning the interstitial Fe had no time to diffuse to precipitation sites, and should therefore be frozen-in, despite being far above the solubility limit at lower temperatures. A second ‘slow’ cool down to 650oC allowed ample time for the Fe to reach the surfaces or other internal precipitation sites. Surprisingly, in both cases the Fe remained in a supersaturated state. This indicates the precipitation process is not diffusion-limited, and that another energetic barrier to precipitate formation must be present. Since the slow cooling used here is similar to the cooling rate experienced by multicrystalline ingots after crystallisation, this precipitate-impeding mechanism is probably responsible for the surprisingly high interstitial Fe concentrations often found in as-grown multicrystalline silicon wafers.
منابع مشابه
Studying precipitation and dissolution of iron in multicrystalline silicon wafers during annealing
In this paper we study the changes in iron concentrations and distributions in multicrystalline silicon (mc-Si) wafers after annealing in the temperature range of 600-900 o C. The dissolved Fe distributions across mc-Si wafers are obtained by photoluminescence imaging taken before and after dissociation of FeB pairs. The results show that the precipitation of dissolved Fe, both near the grain b...
متن کاملIron-rich particles in heavily contaminated multicrystalline silicon wafers and their response to phosphorus gettering
Heavily contaminated multicrystalline silicon wafers have been studied using a scanning synchrotron x-ray fluorescence micro-probe, revealing the presence of iron-rich particles located along grain boundaries. These particles were found to be partially dissolved and removed during phosphorus gettering treatments at 900 or 1000 ◦C for times of up to 100 min, with increased gettering efficiency a...
متن کاملPrecipitation of interstitial iron in multicrystalline silicon
The internal gettering of iron in silicon via iron precipitation at low processing temperatures is known to improve solar cell efficiencies. Studies have found that the optimal temperature lies in the range of 500 o C-600 o C. In this paper, we present experimental results on quantitatively analysing the precipitation of interstitial Fe in multicrystalline silicon wafers during the 500 o C-600 ...
متن کاملIncreasing minority carrier lifetime in as-grown multicrystalline silicon by low temperature internal gettering
(2016) Increasing minority carrier lifetime in as-grown multicrystalline silicon by low temperature internal gettering. Copyright and reuse: The Warwick Research Archive Portal (WRAP) makes this work of researchers of the University of Warwick available open access under the following conditions. This article is made available under the Creative Commons Attribution 4.0 International license (CC...