Nanocoating of natural cellulose fibers with conjugated polymer: hierarchical polypyrrole composite materials.
نویسندگان
چکیده
Astonishingly uniform polypyrrole nanocoating on morphologically complex cellulosic substances was achieved without disrupting the hierarchical network structures of individual cellulose fibers by means of polymerization-induced adsorption.
منابع مشابه
Experimental and modeling investigation of cellulose nanocrystals polymer composite fibers
Chen, Si. Ph.D., Purdue University, May 2015. Experimental and Modeling Investigation of Cellulose Nanocrystal Polymer Composite Fibers. Major Professor: R. Byron Pipes. Cellulose nanocrystals (CNCs) are a class of newly developed and sustainable nanomaterial derived from cellulose-based materials such as wood. There have been substantial research efforts to utilize these materials as reinforci...
متن کاملAll-Cellulose Composite Fibers Obtained by Electrospinning Dispersions of Cellulose Acetate and Cellulose Nanocrystals
All-cellulose composite fibers were produced by electrospinning dispersions containing cellulose acetate (CA) and cellulose nanocrystals (CNCs). Precursor polymer matrices were obtained after dispersion of CA with different degrees of substitution in a binary mixture of organic solvents. The obtained fibers of CA loaded with CNCs had typical widths in the nanoand micro-scale and presented a gla...
متن کاملIonic motion in polypyrrole-cellulose composites: trap release mechanism during potentiostatic reduction.
This work investigates the movement of anions during potentiostatic controlled reduction of novel composite materials consisting of high surface area cellulose substrates, extracted from the Cladophora sp. algae, coated with thin ( approximately 50 nm) layers of the intrinsically conducting polymer (ICP) polypyrrole. The coating was achieved by chemical polymerization of pyrrole on the cellulos...
متن کاملA Nanocellulose Polypyrrole Composite Based on Microfibrillated Cellulose from Wood
It is demonstrated that it is possible to coat the individual fibers of wood-based nanocellulose with polypyrrole using in situ chemical polymerization to obtain an electrically conducting continuous high-surface-area composite. The experimental results indicate that the high surface area of the water dispersed material, to a large extent, is maintained upon normal drying without the use of any...
متن کاملThe Role of Polypyrrole in Electrical Properties of ZnO-Polymer Composite Varistors
Composite films on the base of ZnO with different weight percentages of polypyrrole have been prepared using the hot pressing method and their current-voltage characteristics have been studied. Results show that the films have nonlinear varistor behavior and can be used to protect sensitive circuits from 110V up to 350V overvoltages. It is found that the higher the content...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Chemical communications
دوره 13 شماره
صفحات -
تاریخ انتشار 2005