Effects by sintering on the energy dissipation efficiency in collisions of grain aggregates
نویسنده
چکیده
Energy dissipation on collisions of grain aggregates is investigated taking into account effects by sintering. It is shown that sintering significantly reduces the energy dissipation efficiency because contacts between adjacent grains become strong by sintering.
منابع مشابه
Experimental Study of the Effect of Gabion Structure on the Energy Dissipation of Submerged Hydraulic Jump Downstream of Ogee Spillway
In the last decade, the use of gabion structures in hydraulic engineering for stabilizing the structure due to its high density and weight has become widespread. Also, the material's roughness and porosity cause it to be used in energy dissipation and drainage projects. This study evaluates the relative energy dissipation of gabion structures downstream of the ogee spillway in the conditions of...
متن کاملEffect of milling time and microwave sintering on microhardness and electrical properties of nano and micro structured cordierite
The purpose of this research is to investigate the mechanical and electrical properties of nano structured cordierite. Nano grain size powders were synthesized through mechanical activation by high-energy ball milling of the starting powders containing 34.86 wt% Al2O3, 51.36 wt% SiO2, and 13.78 wt% MgO. Samples were prepared by conventional and microwave sintering at 1390°C. SEM observations il...
متن کاملGrain growth kinetic of spark plasma sintered magnesia
In this research, the densification of magnesia nanopowder with a mean particle size of about 100 nm was investigated by spark plasma sintering undera pressures of 80 MPa and at temperature range from 1000 °C to 1400 °C and a heating rate of 50 °C/min for 20 minutes. The density of the samples slowly increased with increasing sintering temperatures to 1200 °C. Afterwards, with more increasing o...
متن کاملEffects of the sintering temperature on the flux-pinning mechanism and the activation energy of malic-acid doped MgB2
The flux-pinning mechanism and activation energy of 10 wt % malic acid-doped MgB2 were investigated by measuring of the critical current density and resistivity as a function of magnetic field and temperature. A crossover field, Bsb, was observed from the single vortex to the small vortex bundle pinning regime. For the sintered sample, the temperature dependence of Bsb(T) at low temperature i...
متن کاملFabrication of Nanostructured Cu matrix Nanocomposites by High Energy Mechanical Milling and Spark Plasma Sintering
Spark plasma sintering (SPS) is a sintering process that is capable of sintering hard worked powders in short times. This technique was used to fabricate bulk Cu and Cu-SiC nanocomposites. Pure Cu and mixed powders of Cu including 4 vol% of SiC nanoparticles were mechanically alloyed for 25 h and sintered at 750˚C under vacuum condition by SPS method. Microstructures of the materials were chara...