The Effect of the Third Element Cr on Oxidation Behavior of Fe - x Cr - 10 Al ( at . % ) Alloys at 900 o C
نویسندگان
چکیده
Alloys Fe-(0, 5, 10)Cr-10Al (all in at.%) were oxidized at 900 o C in 1 atm oxygen to study the effect of Cr additions on the oxidation behavior. The oxidation kinetics was recorded with a thermal microbalance. The morphologies and microstructures of the oxide scales were examined using SEM, EDS, and XRD. Fe-10Al developed an Al2O3-rich scale during the initial stage of oxidation, and a non-protective scale containing oxides of Fe and Al formed. Mixed oxides of Al and Fe formed firstly on Fe-5Cr-10Al, but an externally dense and continuous Al2O3-rich scale formed. The initially formed Fe oxides were locally reduced to Fe-rich particles. Fe-10Cr-10Al formed an Al2O3-rich scale from the onset of oxidation and this slowly growing scale was protective up to 50 h. The Cr additions to Fe-10Al were beneficial for restraining the oxidation of Fe, but that did not promote the transition from metastable Al2O3 to -Al2O3.
منابع مشابه
The Effect of Nickel Increasing and Aluminum Addition on Sulfidation Resistance of Fe-Ni-Cr Alloys (TECHNICAL NOTE)
In this research the effects of; increasing the amount of nickel and adding aluminum to create and prolong sulfidation resistance of Fe-Ni-Cr alloys have been investigated. Sulfidation tests were carried out at 1100°C in S/O bearing atmosphere. Prior to the tests, the specimens were annealed in argon at 1250°C for 8 hrs. Weight changes were measured and corroded deposits were analyzed byscannin...
متن کاملThe effect of Y and Ti on FeCrAl oxidation at 1400 C
Inco alloy MA956 (Fe-20wt%Cr-4.5%Al-0.35%Ti + 3~01% Y203-A1203) was oxidized in 1 atm of dry, flowing O2 at 1400 OC. Good scale-metal adhesion was observed. Some spalling occurred upon cooling, but it remained within the oxide, not through to the bare metal. Cyclic experiments showed good scale adherence. Y was found to segregate to the oxide grain boundaries and by implication to have modified...
متن کاملThe effect of reactive element coatings on the oxidation behaviour of pure Cr and high Cr-content alloys at 900 °C
The influence of various reactive element (RE) oxide coatings ( Y 2 0 3 , Ce02, La203, CaO and Hf02) on the oxidation behaviour of pure Cr, Fe26Cr and Ni25Cr at 900 OC in oxygen at 5 x torr has been investigated using the 1 8 0 / ~ 1 ~ ~ technique. Polished samples were reactively sputter-coated with 4 nm of the RE oxide and subsequently oxidized sequentially in 1 6 0 2 and then in " 0 2 . The ...
متن کاملSynthesis of Nanostructure Ti-45Al-5Cr Alloy by Mechanical Alloying and Study the Effect of Cr Addition on Microstructure of TiAl Alloy
In this work, mechanical alloying was employed to produce Ti-50Al and Ti-45Al-5Cr (at%) alloys. Alloying was performed in a planetary mill and the alloying time varying from 5 to 70h. Characterization of the powder mixture was performed by X-ray diffraction (XRD), SEM analyses and DTA test, during mechanical alloying and after annealing at 1100°c in vacuum oven. The results showed, after 50h of...
متن کاملEffect of surface-applied reactive elements on the early stage oxidation of Fe- 18Cr-5Al and Fe-18Cr-5Al-1Hf alloys
The effect of lanthanum implantation on the early stage oxidation of Fe-18wt%Cr5wt%Al and Fe-l8wt%Cr-5wt%Al-Iwt%Hf alloys at 1100 OC has been investigated. I t was found that the reactive element enriched surfaces oxidized almost two times faster initially, and the scale that formed had a higher iron content. An extremely wavy scale/alloy interface developed in the early stage due to the accele...
متن کامل