IJESRT INTERNATIONAL JOURNAL OF ENGINEERING SCIENCES & RESEARCH TECHNOLOGY Zn - Ni Alloy Deposit for Cadmium Replacement Applications
نویسندگان
چکیده
Zinc nickel alloy was deposited from alkaline bath at a PH of 13-14 with the nickel percentage of 5-9% in our prior research. Present study dealt with the research on 10-12% of Nickel at a PH of 12-13 from Zinc – nickel alloy electrolyte and the remaining percentage of Zinc, required for corrosion resistant applications to be used for reliable alternative of cadmium. Hull cell studies was carried out to optimize current density, temperature, agitation etc., for getting a deposition of 10-12% of Ni & 88-90 % of Zn. SEM, EDAX, XRD measurements characterize the deposit properties and structure. Corrosion resistance measurements such as polarisation, corrosion impedance spectra of zinc-nickel alloy were evaluated.
منابع مشابه
Development of a New Electrodeposition Process for Plating of Zn-Ni-X (X5Cd, P) Alloys I. Corrosion Characteristics of Zn-Ni-Cd Ternary Alloys
A new Zn-Ni-Cd plating process was developed which offers a unique way of controlling and optimizing the Ni and Cd contents in the final deposit. Zinc-nickel-cadmium alloy was deposited from a 0.5 M NiSO4 1 0.2 M ZnSO4 bath in the presence of 0.015 M CdSO4 and 1 g/L nonyl phenyl polyethylene oxide. Using this process a Zn-Ni-Cd ternary alloy, with a higher nickel content as compared to that obt...
متن کاملA Novel Electrodeposition Process for Plating Zn-Ni-Cd Alloys
Zn-Ni-Cd alloy was electrodeposited from an alkaline electrolytic bath under potentiostatic conditions. Bath analyses using a pH concentration diagram reveal that addition of a complexing agent is essential to maintain the bath stability. Introduction of a low concentration of CdSO4 reduces the anomalous nature of the Zn-Ni deposit. Deposits obtained from the electrolytic bath which contains 60...
متن کاملMetallurgical consideration on the calibration curve for binary alloy samples in low-pressure argon laser-induced plasma spectrometry.
The composition dependence of the emission intensities was investigated in Cu-Ni as well as Ni-Zn binary alloy samples when a low-pressure argon laser-induced plasma was employed as the excitation source. The calibration curve in the Cu-Ni alloy system gave a linear relationship, implying that the selective evaporation of Cu or Ni atoms was caused less in those alloys having several chemical co...
متن کاملCorrosion Protection of Steel Using Nonanomalous Ni-Zn-P Coatings
A novel technique for obtaining nonanomalous Ni-Zn-P coatings with high Ni content ~74 wt % as compared to 15-20 wt % in the conventional plating method! has been developed. These coatings show promise as a replacement for Cd in sacrificially protecting steel. Ni-Zn-P coatings were deposited using an electroless method from a solution containing NiSO4 , complexing agent and ammonium chloride. V...
متن کاملExtraction of Zn, Mn and Co from Zn-Mn-Co-Cd-Ni containing solution using D2EHPA, CYANEX® 272 and CYANEX® 302
Effects of pH, D2EHPA, Cyanex® 302 and Cyanex® 272 on extractions of zinc, manganese and cobalt from a Zn-Mn-Co-Cd-Ni containing solution was comprehensively investigated at the room temperature. The addition of Cyanex® 302 indicated a left-shifting-effect on the extraction curve of zinc, a right-shifting-effect on the extraction curve of manganese and no effect on the extraction of cobalt. The...
متن کامل