Microstructure and Fatigue Characteristic of AM60B Magnesium Alloy
نویسنده
چکیده
This paper summarizes and reviews the findings of our research on AM60B magnesium alloy conducted in past 8 years. It essentially covers three categories: microstructural study, environmental effect, and fatigue crack growth rate of AM60B. The experimental and numerical studies on the influence of casting defects on this particular material’s properties are reviewed in the first part. It has been shown that the non-uniform solidification of the casting results in variations of the microstructure in different layers (skin and core) of the alloy which affects the mechanical properties in those regions. Moreover, the influence of microstructure on fatigue crack initiation and propagation response of the alloy is presented. The influence of several casting defects on the failure mechanism of the material are also numerically analyzed and discussed. The influence of elevated and cold temperatures on the fatigue response of the alloy is reviewed in the second part. Our findings show that the temperature does not have a significant effect on the number of cycles to failure. However, but at some stress level, this effect cannot be dismissed. The fatigue crack growth rate (FCGR) response of the alloy at a wide range of stress ratios is also investigated in the last part. The FCGR of the alloy showed a noticeable dependency on the stress ratio. A model is proposed for estimating the FCGR of the alloy, which could provide a good prediction of alloy’s FCGR over a wide range of negative and positive stress ratios. The integrity of the new model is also compared against other models. Finally, the influence of compressive loading on fatigue life of the specimens under constant and random amplitude cyclic loading is investigated experimentally. OPEN ACCESS
منابع مشابه
Scatter Analysis of Fatigue Life and Pore Size Data of Die-Cast AM60B Magnesium Alloy
Scatter behavior of fatigue life in die-cast AM60B alloy was investigated. For comparison, those in rolled AM60B alloy and die-cast A365-T5 aluminum alloy were also studied. Scatter behavior of pore size was also investigated to discuss dominant factors for fatigue life scatter in die-cast materials. Three-parameter Weibull function was suitable to explain the scatter behavior of both fatigue l...
متن کاملFATIGUE BEHAVIOUR OFA ROLLED AZ31 MAGNESIUM ALLOYS PREPARED BY EPAND BB CONDITIONS
Abstract: Rotating bending fatigue tests have been performed using smooth specimens of a rolled AZ31 magnesium alloy in laboratory air at ambient temperature. Fatigue strength and characteristic was evaluated and fracture mechanism was discussed on the basis fracture surface analysis. Electrical polishing (EP) as well as deep rolling (ball burnishing (BB)) U-notched specimens were performed on ...
متن کاملImprovement of Fatigue Strength of Light Metallic Materials by Cavitation Shotless Peening
Cavitation normally causes severe damage in hydraulic machinery such as pumps, valves and so on. However, cavitation impact can be utilized to surface treatment to improve fatigue strength of metallic materials in the same way as shot peening. A peening method using cavitation impact was named as “cavitation shotless peening” or “cavitation peening” as shots are not required. As increase of sur...
متن کاملRatcheting crystal plasticity modeling in microstructure of magnesium alloy under stress-controlled cyclic tensile loading with non-zero mean stress
Todays, the requirement of lowering the vehicle weight for the reduction of the fuel consumption and emissions, one of the methods considered by designers is to use the ligh magnesium alloy under cylclic loadings. In this article, considering the microstructure of the AZ91D magnesium alloy, its crystalline structure, a model for predicting the ratcheting behavior of this alloy was adapted and v...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2012