Effects of cold-rolling deformation on texture evolution and mechanical properties of Ti-29Nb-9Ta-10Zr alloy

The crystallographic texture of Ti–29Nb–9Ta–10Zr alloy is studied after cold-rolling with different amounts of thickness reduction, up to 60%. The major texture components developed during cold-rolling were: γ-fibre components: {111}〈 〉, {111}〈 〉, {111}〈 〉 and {111}〈 〉; texture component: {112}〈 〉 and texture components: {001}〈 〉 and {010}〈001〉. Besides crystallographic texture the resulted mechanical properties were studied by nanoindentation. It was showed that the decrease in Young's modulus after different cold-rolling stages is mainly attributed to the stress-induced α′′-Ti phase formation. At 60% cold-rolling thickness reduction obtained an elastic modulus close to 45.29±3.81 GPa, coupled with an average Vickers microhardness close to 279.83±4.28 HV.