White Light-Emitting Diodes Based on AgInS2/ZnS Quantum Dots with Improved Bandwidth in Visible Light Communication

نویسندگان

  • Cheng Ruan
  • Yu Zhang
  • Min Lu
  • Changyin Ji
  • Chun Sun
  • Xiongbin Chen
  • Hongda Chen
  • Vicki L. Colvin
  • William W. Yu
چکیده

Quantum dot white light-emitting diodes (QD-WLEDs) were fabricated from green- and red-emitting AgInS₂/ZnS core/shell QDs coated on GaN LEDs. Their electroluminescence (EL) spectra were measured at different currents, ranging from 50 mA to 400 mA, and showed good color stability. The modulation bandwidth of previously prepared QD-WLEDs was confirmed to be much wider than that of YAG:Ce phosphor-based WLEDs. These results indicate that the AgInS₂/ZnS core/shell QDs are good color-converting materials for WLEDs and they are capable in visible light communication (VLC).

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Thin-film Encapsulation of Organic Light-Emitting Diodes Using Single and Multilayer Structures of MgF2, YF3 and ZnS

In this research, the lifetime of green organic light emitting diodes (OLEDs) is studied using four passivation layers. To encapsulate the OLEDs, MgF2, YF3, composed of alternating MgF2/ZnS and YF3/ZnS layers were grown by thermal vacuum deposition. Measurements show that the device lifetime is significantly improved by using YF3 and ZnS as passivation layers. However, diodes encapsulated by Mg...

متن کامل

Further Improvement in Efficiency of ZnO Nanorod Based Solar Cells Using ZnS Quantum Dots as Light Harvester and Blocking Layer Material

Zinc oxide nanorod arrays (ZnO NRs) were grown on the ZnO seed layers via an aqueous solution using hydrothermal method and their photovoltaic properties were investigated. It was found that the growth period of 20 minutes is the optimum condition for ZnO nanorods growth, the cell containing these nanorods was considered as a reference cell. In order to further increase the cell performance, Zn...

متن کامل

Shifting the light emitting component from core to shell: an effective approach to improve the efficiency of light-emitting diodes based on multi-junction quantum materials.

Herein, using the light emitting component as the inner shell, we construct an advanced quantum-dot-quantum-well structure, ZnCdS/CdSe/CdZnSeS/ZnS, and use it for the fabrication of a light-emitting-diode. In comparison with the device containing conventional structured quantum dots, CdSe/CdZnSeS/ZnS, the advanced device possesses a superior performance in aspects of luminance, current efficien...

متن کامل

Improved efficiencies in organic light emitting diodes made with CdSe/ZnS quantum dots and a semiconducting polymer.

In this study, we report the fabrication and characterization of organic/inorganic hybrid polymer light emitting diodes (PLEDs) made with ZnS-capped CdSe core/shell type nanocrystals and a light-emitting polymer poly[2-phenyl-3-(9,9-dihexylfluoren-2-yl)-1,4-phenylene vinylene]-co-[2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenylene vinylene]. The device using pristine polymer as active layer emitted y...

متن کامل

Critical role of CdSe nanoplatelets in color-converting CdSe/ZnS nanocrystals for InGaN/GaN light-emitting diodes.

Here we report CdSe nanoplatelets that are incorporated into color-converting CdSe/ZnS nanocrystals for InGaN/GaN light-emitting diodes. The critical role of CdSe nanoplatelets as an exciton donor for the color conversion was experimentally investigated. The power conversion efficiency of the hybrid light-emitting diode was found to increase by 23% with the incorporation of the CdSe nanoplatele...

متن کامل

ذخیره در منابع من

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2016