Research on Chloride Penetration Resistance of Hybrid Fiber Reinforced Self-Compacting Concrete
نویسندگان
چکیده
The properties of chloride penetration of hybrid fiber reinforced self-compacting concrete (SCC) were investigated in this study. The results show that the chloride penetration resistance of concrete can be improved by single incorporation either carbon or cellulose fibers. The concrete chloride diffusion coefficient DRCM of 12-cm length carbon SCC with fiber content of 1.7, 2.72, and 3.4 kg/m3 decreases by 10.3, 25.5, and 18.2% compared to reference concrete without any fibers, respectively. Moreover, the concrete chloride diffusion coefficient DRCM of cellulose SCC with fiber content of 1.2, 1.6, and 2.0 kg/m3 decreases by 18.8, 22.4, and 26.7% compared to reference concrete, respectively. Based on the results of orthogonal experimental design, the chloride diffusion coefficients DRCM of hybrid fiber reinforced SCC are listed in order of importance, as follows: length of carbon fiber > content of carbon fiber > content of cellulose fiber; furthermore, the hybrid of 2.72-kg/m3 carbon fiber with length of 12 mm and 2.0-kg/m3 cellulose fiber exhibits the most significant effect on chloride diffusion coefficients DRCM of SCC.
منابع مشابه
Evaluation of Hybrid Fiber Reinforced Concrete Exposed to Severe Environmental Conditions
Hybrid fiber reinforced concrete (HFRC) consisting of two or more different types of fibers has been widely investigated because of its superior mechanical properties. In the present study, the effect of the addition of steel (0.25%, 0.5%, 0.75%, and 1% of concrete volume) and Polypropylene (0.2%, 0.4%, and 0.6% of concrete volume) fibers on the surface scaling resistance of concrete, depth of ...
متن کاملComparison of Permeability and Drying Shrinkage of Self Compacting Concrete Admixed with Wollastonite Micro Fiber and Flyash
Cement substitution in self compacting concrete (SCC) is emphasized to conserve environment, reduce cost and utilize waste materials. This paper focuses on comparing the permeability and drying shrinkage of SCC containing Wollastonite micro fiber (WMF), a cheap pozzolanic fiber with respect to flyash. Microsilica was added for providing required viscosity to maintain homogeneity of the mixes. T...
متن کاملDurability of Self-compacting Lightweight Aggregate Concretes (LWSCC) as Repair Overlays
For rehabilitation of damaged concrete structures, the durability of repair overlay is a very important issue. Self-compacting concretes (SCC) are known as a suitable repair overlay materials. In this study, the durability of different self-compacting lightweight aggregate concretes (LWSCC) and effect of lightweight aggregate type on them is investigated. 3 mix designs of LWSCC containing three...
متن کاملStudy of effect of paste volume, water to cementitious materials and fiber dosages on rheological properties and in-situ strength of self-compacting concrete
As a vibration- free concrete, self- compacting concrete (SCC) can be easily used in the absence of consolidation, therefore; it is a good option for repairing and retrofitting concrete structures. The quality of repair layer is highly effective on a successful repair. Accordingly, in this study, factors affecting the quality of fiber-reinforced self-compacting concrete repair layer, including ...
متن کاملHybrid Fiber Reinforced Concrete Containing Pumice and Metakaolin
Fiber reinforced concrete (FRC) has been widely used due to its advantages over plain concrete such as high energy absorption, post cracking behaviour, flexural and impact strength and arresting shrinkage cracks. But there is a weak zone between fibers and paste in fiber reinforced concretes and this weak zone is full of porosity, especially in hybrid fiber reinforced concretes. So it is necess...
متن کامل