Estimation of Atmospheric Corrosion of High-Strength, Low-Alloy Steels

نویسندگان

  • S. Vaynman
  • R. S. Guico
  • M. E. Fine
  • S. J. Manganello
چکیده

This data analysis was undertaken to investigate the weatherability of steels whose compositions do not fall in the range of ASTM Standard G101, Estimating the Atmospheric Corrosion Resistance of Low-Alloy Steels (1). This standard was developed to estimate the corrosion resistance of low-alloy weathering steels from chemical composition data and from actual atmospheric exposure tests. This standard is limited to steels within the composition range outlined in TABLE 1.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

How to make N2 listen to you in steel making!

All steels contain some amount of dissolved gases such as oxygen, hydrogen and nitrogen of which nitrogen is effective in improving the mechanical and corrosion properties of stainless steels if it remains in solid solution or precipitates as very fine and coherent nitrides or carbo-nitrides with iron or alloying elements. When nitrogen is added to austenitic steels it can simultaneously improv...

متن کامل

Rust Formation Mechanism on Low Alloy Steels after Exposure Test in High Cl− and High SOx Environment

Exposure tests were performed on low alloy steels in high Cl- and high SOx environment, and the structure of the rust were analyzed by TEM (Transmission Electron Microscopy) and Raman Spectroscopy. In the exposure test site, the concentrations of Cl- and SOx were found to be high, which caused the corrosion of the steels. The conventional weathering steel (SMA: 0.6% Cr-0.4% Cu-Fe) showed higher...

متن کامل

Modeling of Corrosion-Fatigue Crack Growth Rate Based on Least Square Support Vector Machine Technique

Understanding crack growth behavior in engineering components subjected to cyclic fatigue loadings is necessary for design and maintenance purpose. Fatigue crack growth (FCG) rate strongly depends on the applied loading characteristics in a nonlinear manner, and when the mechanical loadings combine with environmental attacks, this dependency will be more complicated. Since, the experimental inv...

متن کامل

The Evaluation of Corrosion Behavior of AISI 347 Stainless Steel to ASTM A335 Low Alloy Steel Dissimilar Welds

In the present study, the corrosion behavior of AISI 347 austenitic stainless steel to ASTM A335 low alloy steel dissimilar joint was investigated. For this purpose, two filler metals, ER309L and ERNiCr-3, were selected to be used during the gas tungsten arc welding process. To investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solu...

متن کامل

Effect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature

The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO₂ environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO₂ and H₂S coexistence conditions, the corrosion behavior of low-chromium steels in CO₂-H₂S environment with high pressure and high temperature was investigated using weight loss m...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2002