Microstructure and Sliding Wear Behaviour of In-Situ TiC-Reinforced Composite Surface Layers Fabricated on Ductile Cast Iron by Laser Alloying
نویسنده
چکیده
TiC-reinforced composite surface layers (TRLs) on a ductile cast iron EN-GJS-700-2 grade (DCI) substrate were synthesized using a diode laser surface alloying with a direct injection of titanium powder into the molten pool. The experimental results were compared with thermodynamic calculations. The TRLs having a uniform distribution of the TiC particles and their fraction up to 15.4 vol % were achieved. With increasing titanium concentration in the molten pool, fractions of TiC and retained austenite increase and the shape of TiC particles changes from cubic to dendritic form. At the same time, the cementite fraction decreases, lowering the overall hardness of the TRL. A good agreement between experimental and calculated results was achieved. Comparative dry sliding wear tests between the as-received DCI, the TRLs and also laser surface melted layers (SMLs) have been performed following the ASTM G 99 standard test method under contact pressures of 2.12 and 4.25 MPa. For both the as-received DCI and the SMLs, the wear rates increased with increasing contact pressure. The TRLs exhibited a significantly higher wear resistance than the others, which was found to be load independent.
منابع مشابه
Tribological Behavior of Reinforced and Unreinforced High Chromium Cast Iron
In this paper, the metal matrix composites containing 22 wt % Cr, 2.5 wt % C and 2 to 16 volume percent TiC were processed by solidifying Fe-Cr-Ti-C in which precipitation of titaniumcarbide and chromium carbide occurred. The microstructure and abrasion resistance of in-situ synthesized composites were compared with the unreinforced high chromium white cast iron (HCWCI) containing 22 w. t. % C...
متن کاملTiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding
In this study, a TiC-reinforced composite coating was produced to improve the wear resistance of a pearlite matrix grey iron using a pre-placed Ti powder by laser cladding. Results of scanning electron microscopy (SEM), X-ray diffractometer (XRD), and energy dispersive X-ray spectroscopy (EDS) confirmed that the coating was composed of TiC particles and two kinds of α-Fe phase. The fine TiC par...
متن کاملPLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE
An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (`3-^9) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction....
متن کاملStructural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملProduction of Dispersed Ceramic Nano-Particles in Al Alloy Using Friction Stir Processing
In this research, surface composite layers containing nano sized TiB2, Al2O3-TiB2, ZrO2 and CNT particles have been fabricated on Aluminum alloy substrates by friction stir processing. The effects of different processing variables such as number of passes and strengthening particle distribution, hardness, and wear properties of surface nano...
متن کامل