Bond strengths of three different dentin adhesive systems to sclerotic dentin.
نویسندگان
چکیده
The two-fold aims of this study were: (1) to evaluate the microtensile bond strengths of different adhesive systems to sclerotic and sound palatal dentin; and (2) to observe the respective resin-dentin interfaces. Thirty extracted human incisor teeth were divided into two groups. Group I comprised sclerotic defects in the palatal zone. Group II comprised sound palatal dentin surfaces as control. Each group (n=15) was divided into three subgroups according to dentin adhesive systems: self-etch (Clearfil SE Bond), total-etch (Scotchbond Multi-Purpose Plus), and glass ionomer (Reactmer Bond) adhesive systems. The specimens were subjected to tensile forces. Obtained data were analyzed by two-way ANOVA and post hoc Duncan's test. Fracture sites and resin-dentin interfaces were observed using a light microscope and SEM. With sound dentin, Clearfil SE Bond showed a significantly higher bond strength than the other adhesives (p < 0.05). With sclerotic dentin, although there were no significant differences in bond strength among the adhesives groups (p > 0.05), the bond strength values of Clearfil SE Bond and Scotchbond Multi-Purpose Plus were significantly decreased. On resin-dentin interface observation, different images were presented by different bonding systems.
منابع مشابه
In vitro bond strengths and SEM evaluation of dentin bonding systems to different dentin substrates.
In comparison to enamel, bonding to normal dentin is a greater challenge because of its organic constituents, fluid-filed tubules, and variations in intrinsic composition. Bonding to sclerotic dentin is even more difficult. To evaluate the shear bond strengths of four adhesive systems to dentin substrates with different levels of mineralization, 120 extracted human teeth were randomly assigned ...
متن کاملEffect of salivary contamination on shear bond strength of three different dentin adhesive systems
Effect of salivary contamination on shear bond strength of three different dentin adhesive systems Dr. H. Kermanshah* - Dr. H. Haj miragha** - Dr. SH. Gatoeizadeh*** *- Assistant Professor of Operative Dentistry Dept. - Faculty of Dentistry – Tehran University / Medical Sciences. **- Assistant Professor of Fixed Prosthodontics Dept. & Dental Research Center - Faculty of Dentistry – Tehran Unive...
متن کاملMicroscopy comparative evaluation of the SE systems adhesion to normal and sclerotic dentin.
The purpose of this study was in vitro evaluation and comparison of the adhesion of self-etch (SE) adhesive systems applied on normal and sclerotic dentin. For this study, Class 5 cavities were prepared on sound teeth as well as on teeth with sclerotic dentin. They were then restored by means of the SE 2-step OptiBond XTR (Kerr) and SE 1-step Bond Force (Tokuyama Dental) adhesive systems, as we...
متن کاملاستحکام باند برشی آمالگام به عاج با استفاده از سیستمهای چسبنده عاجی
Background and Aims: The aim of this in vitro study was to assess the shear bond strength of amalgam to dentin using four dentin adhesive systems.Materials and Methods: One hundred human molars were selected. After enamel removal, a dentin cylinder with 3 mm thickness was prepared. Eighty specimens were resorted with amalgam and four dentin adhesive systems as follows (n=20): group 1, Scotch Bo...
متن کاملبررسی اثر برداشت کلاژن بر میزان استحکام باند برشی چهار سیستم باند عاجی یک جزئی
Background and Aim: Achieving adhesion between restorative materials and dentin as a wet and dynamic surface is an important topic in restorative and especially in conservative dentistry. Adhesion of new dentin bonding systems depends on the formation of hybrid layer and micromechanical retention. Nevertheless, an ideal adhesive system has not yet been introduced .Recent studies reveal an incre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 27 3 شماره
صفحات -
تاریخ انتشار 2008