High-Pressure Synthesis and Crystal Structure of Ce4B14O27
نویسندگان
چکیده
Ce4B14O27 was synthesized under conditions of 2.6 GPa and 750 °C in a Walker-type multianvil apparatus. The crystal structure was determined on the basis of single-crystal X-ray diffraction data, collected at room temperature, revealing that Ce4B14O27 is isotypic to La4B14O27. Ce4B14O27 crystallizes monoclinically with four formula units in the space group C2/c (No. 15) and the lattice parameters a = 1117.8(2), b = 640.9(2), c = 2531.7(5) pm, and β = 100.2(1)°. The three-dimensional boron-oxygen framework consists of [BO4]5- tetrahedra and trigonal-planar [BO3]3- groups. The structure contains two crystallographically different cerium ions. Furthermore, Raman spectroscopy was performed on single crystals of Ce4B14O27.
منابع مشابه
SYNTHESIS AND CRYSTAL STRUCTURE OF [Pph ] [WS (CUNCS) ] A. Taeb A. Beheshti and N.K. Javadi SYNTHESIS AND CRYSTAL STRUCTURE OF [Pph ] [WS (CUNCS) ]
The crystals of [WS (CuNCS) ] anion have been isolated from CH ,CI solution and examined by X-ray structural analysis as well as by IR spectroscopy. The unit cell is monoclinic with a= 14.3796(13), b= 18.039(1 I), c= 22.5956(23)& P= 96.053(8)', space group P2,/n (14), Z= 4. The crystal structure was refined by the least-squares calculations to a final R-value of 0.0398(Rw= 0.0443) for 2777 u...
متن کاملInfluence of Calcination Kinetics Parameters on Synthesis of KNN Piezoelectric Ceramics
The current research was focused on synthesizing potassium sodium niobate (KNN) piezoelectric ceramics for the system (K0.48Na0.52) NbO3 by high energy ball milling process for 15h at the speed of 300 rpm. The blended nano-crystalline powder was calcined in conventional box furnace at 700oC, 800oC and 900oC for duration of 5h, 7h and 10h. Diffraction result of calcine powder confirmed the f...
متن کاملSYNTHESIS AND CRYSTAL STRUCTURE OF [PPh ] [WOS (CUNCS) ]
The reaction of [PPhJ, NOS,] with CuCl and KSCN (1 :3:3) in acetone produces the yell-ow crystals of [PPh,], [WOS,(CuNCS),]. The crystals are triclinic, space group P1(2), z=2, a=12.4823(7), b=12.9224(7), c=18.6395(10)?, ?=83.907(5), ?= 73.152(4), Y= 65.194(4)'. The crystal structure was determined by single crystal Xray diffraction methods (Mo-K ?) and refined by least-squares calculations ...
متن کاملOne-dimensional Uranium(VI) Coordination Polymer Complex Containing Dimethyl and Trimethyl Phosphate Ligands: Synthesis, Spectroscopic Characterization, Thermal Analyses, and Crystal Structure
A new one-dimensional uranium(VI) coordination polymer, [UO2(μ-DMP)2(TMP)]n (1) (DMP is dimethyl phosphate and TMP is trimethyl phosphate), was prepared from the reaction of UO2(NO3)2.6H2O and TMP in in THF (THF is tetrahydrofuran) as a solvent. Suitable crystals of this complex for crystal structure determination were obtained by slow evaporation of the produced yellow solution at room tempera...
متن کامل1D Copper(I) Coordination Polymer [Cu(Clba2-1,2-pn)(NCS)]n: Synthesis of Microparticles and Single Crystals, Crystal Structure, and Thermal Study
In this research, 1D four-coordinate copper(I) coordination Polymer [Cu(Clba2-1,2-pn)(NCS)]n (1) with thiocyanate anion as bridging ligand, where Clba2-1,2-pn = N,Nʹ-bis(2,4-chlorobenzylidene)propane-1,2-diamine), was synthesized by slow evaporation of solvent at room temperature and characterized by elemental analysis (CHN) and single-cryst...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 639 شماره
صفحات -
تاریخ انتشار 2013