In situ 3D Imaging of Crack Growth in Dentin
نویسندگان
چکیده
منابع مشابه
The effect of aging on crack-growth resistance and toughening mechanisms in human dentin.
Crack-growth experiments in human dentin have been performed in situ in an environmental scanning electron microscope to measure, for the first time, the crack-growth resistance curve (R-curve) for clinically relevant (<250 microm) crack extensions and to simultaneously identify the salient toughening mechanisms. "Young" dentin from donors 19-30 years in age and "aged" dentin from donors 40-70 ...
متن کاملThe effects of tubule orientation on fatigue crack growth in dentin.
The fracture of restored teeth is a significant obstacle to lifelong oral health. Recent studies suggest that fatigue cracks originate at flaws introduced during cavity preparation and that fatigue crack growth is a principle cause of restored tooth fractures. In this study, the rate of fatigue crack growth in bovine dentin was estimated under mode I cyclic loading. Double cantilever beam (DCB)...
متن کاملFatigue and Fracture of Bovine Dentin
In this paper, the fatigue and fracture properties of bovine dentin are evaluated using in vitro experimental analyses. Double cantilever beam (DCB) specimens were prepared from bovine maxillary molars and subjected to zeroto-tension cyclic loads. The fatigue crack growth rate was evaluated as a function of the dentin tubule orientation using the Paris law. Wedge-loaded DCB specimens were also ...
متن کاملAge, dehydration and fatigue crack growth in dentin.
A preliminary study of the effects from age and dehydration on fatigue crack growth in human dentin was conducted. Compact tension (CT) fatigue specimens of coronal dentin were prepared from extracted molars and subjected to high cycle fatigue (10(5)<N<10(6)) under Mode I loading. Young hydrated dentin (mean age=25+/-7 years), old hydrated dentin (mean age=55+/-14 years) and young dehydrated de...
متن کاملA comparison of fatigue crack growth in resin composite, dentin and the interface.
OBJECTIVES The objective of this in vitro study was to evaluate the fatigue crack growth properties of the dentin/resin adhesive interface. METHODS Compact tension (CT) specimens were prepared from coronal dentin, resin composite, and dentin bonded to resin composite using Optibond Solo Plus adhesive. All specimens were then subjected to cyclic Mode I loading while fully hydrated at a stress ...