Constructing WO3/TiO2 composite structure towards sufficient use of solar energy.
نویسندگان
چکیده
A WO(3)/TiO(2) composite is constructed with the ability to degrade organic molecules under visible irradiation, which is newly explored by UV pre-irradiation. The long lasting visible-light photoactivity and the consecutive photocatalytic process will benefit the efficient use of solar energy.
منابع مشابه
Photocatalytic energy storage ability of TiO2-WO3 composite prepared by wet-chemical technique.
TiO2-WO3 hybrid photocatalysts were prepared using wet-chemical technique, and their energy storage performance was characterized by electrochemical galvanostatic method. TiO2 powder was coupled with WO3 powder, which was used as electron pool and the reductive energy could be stored in. As a result, the prepared TiO2-WO3 had good energy storage ability while pure TiO2 showed no capacity and pu...
متن کاملEnhanced photoelectrochemical and photocatalytic activity of WO3-surface modified TiO2 thin film
Development of nanostructured photocatalysts for harnessing solar energy in energy-efficient and environmentally benign way remains an important area of research. Pure and WO3-surface modified thin films of TiO2 were prepared by magnetron sputtering on indium tin oxide glass, and photoelectrochemical and photocatalytic activities of these films were studied. TiO2 particles were <50 nm, while de...
متن کاملPreparation, characterization and photocatalytic behavior of WO3-fullerene/TiO2 catalysts under visible light
WO3-treated fullerene/TiO2 composites (WO3-fullerene/TiO2) were prepared using a sol-gel method. The composite obtained was characterized by BET surface area measurements, X-ray diffraction, scanning electron microscopy, energy dispersive X-ray analysis, transmission electron microscopy, and UV-vis analysis. A methyl orange (MO) solution under visible light irradiation was used to determine the...
متن کاملOne-Step Formation of WO3-Loaded TiO2 Nanotubes Composite Film for High Photocatalytic Performance
High aspect ratio of WO3-loaded TiO2 nanotube arrays have been successfully synthesized using the electrochemical anodization method in an ethylene glycol electrolyte containing 0.5 wt% ammonium fluoride in a range of applied voltage of 10–40 V for 30 min. The novelty of this research works in the one-step formation of WO3-loaded TiO2 nanotube arrays composite film by using tungsten as the cath...
متن کاملBias-free, solar-charged electric double-layer capacitors.
The conversion of solar energy with simultaneous electric energy storage provides a promising means for optimizing energy utilization efficiency and reducing device volume. In this paper, a 3-dimensional mesoporous carbon coated branched TiO2 nanowire composite is rationally designed for direct conversion and storage of solar energy as electric double-layer capacitive energy. The 1-dimensional,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Chemical communications
دوره 47 14 شماره
صفحات -
تاریخ انتشار 2011