Cohesive zone modeling for structural integrity analysis of IC interconnects
نویسندگان
چکیده
Due to the miniaturization of integrated circuits, their thermo-mechanical reliability tends to become a truly critical design criterion. Especially the introduction of copper and low-k dielectric materials cause some reliability problems. Numerical simulation tools can assist developers to meet this challenge. This paper considers the first bond integrity during wire bond qualification testing. During testing, metal peel off may occur. This mechanical failure mode is caused by delamination of several layers of the interconnect structure. An interfacial damage model is employed for simulating delamination. However, the fact that the considered interfaces are brittle triggers some reported numerical difficulties. This paper illustrates the potential of the interface damage mechanics approach for simulating metal peel off and it highlights the computational aspects to be developed to render a practically applicable approach. 2006 Elsevier Ltd. All rights reserved.
منابع مشابه
An Integrated Platform for Validated Prediction of Collapse of Structures
In developing key documents such as national building codes, regional emergency response plans, and risk management strategies, it is critical to understand the causes and effects of structural collapse. This paper presents ongoing research activities to establish a robust procedure for accurate assessment of the collapse of steel frame structures. A cohesive zone method based strategy is being...
متن کاملA discontinuous Galerkin method for cohesive zone modelling
We propose a discontinuous finite element method for small strain elasticity allowing for cohesive zone modeling. The method yields a seamless transition between the discontinuous Galerkin method and classical cohesive zone modeling. Some relevant numerical examples are presented.
متن کاملTime Domain Analysis of Graphene Nanoribbon Interconnects Based on Transmission Line Model
Time domain analysis of multilayer graphene nanoribbon (MLGNR) interconnects, based on transmission line modeling (TLM) using a six-order linear parametric expression, has been presented for the first time. We have studied the effects of interconnect geometry along with its contact resistance on its step response and Nyquist stability. It is shown that by increasing interconnects dimensions...
متن کاملA Cohesive Zone Model for Crack Growth Simulation in AISI 304 Steel
Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...
متن کاملReview of Damage Tolerant Analysis of Laminated Composites
With advanced composites increasing replacing traditional metallic materials, the material inhomogeneity and inherent anisotropy of such materials lead to not only new attributes for aerospace structures, but also introduce new technology to damage tolerant design and analysis. The deleterious effects of changes in material properties and initiation and growth of structural damage must be addre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Microelectronics Reliability
دوره 47 شماره
صفحات -
تاریخ انتشار 2007