Ultrathin free-standing close-packed gold nanoparticle films: conductivity and Raman scattering enhancement.
نویسندگان
چکیده
A simple filtration technique was developed to prepare large scale free-standing close-packed gold nanoparticle ultrathin films using metal hydroxide nanostrands as both barrier layer and sacrificial layer. As thin as 70 nm, centimeter scale robust free-standing gold nanoparticle thin film was obtained. The thickness of the films could be easily tuned by the filtration volumes. The electronic conductivities of these films varied with the size of the gold nanoparticles, post-treatment temperature, and thickness, respectively. The conductivity of the film prepared from 20 nm gold nanoparticles is higher than that of the film prepared from 40 nm gold nanoparticle by filtering the same filtration volume of their solution, respectively. Their conductivities are comparable to that of the 220 nm thick ITO film. Furthermore, these films demonstrated an average surface Raman scattering enhancement up to 6.59 × 10(5) for Rhodamine 6 G molecules on the film prepared from 40 nm gold nanoparticles. Due to a lot of nano interspaces generated from the close-packed structures, two abnormal enhancements and relative stronger intensities of the asymmetrical vibrations at 1534 and 1594 cm(-1) of R6G were observed, respectively. These robust free-standing gold nanoparticle films could be easily transferred onto various solid substrates and hold the potential application for electrodes and surface enhanced Raman detectors. This method is applicable for preparation of other nanoparticle free-standing thin films.
منابع مشابه
Nanoantenna-assisted plasmonic enhancement of IR absorption of vibrational modes of organic molecules
Nanoantenna-assisted plasmonic enhancement of IR absorption and Raman scattering was employed for studying the vibrational modes in organic molecules. Ultrathin cobalt phthalocyanine films (3 nm) were deposited on Au nanoantenna arrays with specified structural parameters. The deposited organic films reveal the enhancement of both Raman scattering and IR absorption vibrational modes. To extend ...
متن کاملSpontaneous Formation of Fractal Aggregates of Au Nanoparticles in Epoxy-Siloxane Films and Their Application as Substrates for NIR Surface Enhanced Raman Spectroscopy
We present a facile, inexpensive route to free-standing, thermo-mechanically robust and flexible epoxy-siloxane substrates embedded with fractal aggregates of Au nanoparticles, and demonstrate their efficiency as substrates for surface enhanced Raman spectroscopy (SERS) at NIR wavelengths. The metallodielectric films are prepared by generating Au nanoparticles through the in-situ reduction of g...
متن کاملLinker-molecule-free gold nanorod layer-by-layer films for surface-enhanced Raman scattering.
This paper reports a methodology for synthesizing and ordering gold nanorods into two-dimensional arrays at a water/hexane interface. This preparation method allows the systematic control of the nanoparticle film thickness. An investigation into the thickness-dependent surface-enhanced Raman scattering (SERS) of the adsorbed molecules revealed the nanorod (NR) films to have 1 order of magnitude...
متن کاملTwo-dimensional ultrathin gold film composed of steadily linked dense nanoparticle with surface plasmon resonance
UNLABELLED BACKGROUND Noble metallic nanoparticles have prominent optical local-field enhancement and light trapping properties in the visible light region resulting from surface plasmon resonances. RESULTS We investigate the optical spectral properties and the surface-enhanced Raman spectroscopy of two-dimensional distinctive continuous ultrathin gold nanofilms. Experimental results show ...
متن کاملGold nanoparticles on polarizable surfaces as Raman scattering antennas.
Surface plasmons supported by metal nanoparticles are perturbed by coupling to a surface that is polarizable. Coupling results in enhancement of near fields and may increase the scattering efficiency of radiative modes. In this study, we investigate the Rayleigh and Raman scattering properties of gold nanoparticles functionalized with cyanine deposited on silicon and quartz wafers and on gold t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nanoscale
دوره 3 9 شماره
صفحات -
تاریخ انتشار 2011