Wet ball milling was used to exfoliate MoS2. The aim of the study was to examine how the surface energy of all the individual materials affected the formation of the nano‐ sheets. Two types of milling balls were selected: one made of steel and one made of Al2O3. The liquids used were water (H2O), isopropyl alcohol (C3H8O) and kerosene. The obtained nanosheets were identified and characterized using transmission/scanning electron microscopy and electron diffraction. Following sedimentation, scattered light intensity was measured. Our experiments showed that the material of the milling balls played a significant role in the experiment and had an influence on the number of the nanosheets obtained. Irrespective of the liquid employed, the number of nanosheets in the suspension obtained by milling with Al2O3 balls was greater by 100% than those obtained via milling with steel balls.
منابع مشابه
EFFECT OF MECHANICAL ACTIVATION ON THE KINETICS OF LEACHINGOFCHALCOPYRITE IN THE FERRIC SULFATE MEDIA
Abstract: has been investigated. It has been shown that the mechanism of leaching reaction is diffusion through the product layerand does not undergo any change as a result of mechanical activation in a wide range of experimental conditions.Leaching rate is strongly influenced by milling intensity and the effect of ball to powder mass ratio is stronger thanmilling time. Curve fitting of experim...
متن کاملGrinding-aid effect on the colour properties (Ry, whiteness and yellowness) of calcite in stirred media milling
This study investigates the influence of some chemical additives such as methanol, ethanol, sodium oleat, chloroform and sodium hexametaphosphate (SHMP) on the dry fine grinding of calcite (X50= 33 µm) using a stirred media mill. The experiments were carried out by a batch operation, and the change in colour properties (Ry, whiteness and yellowness) of calcite powder. The results showed that th...
متن کاملTHE EFFECT OF MILLING CONDITIONS ON THE MECHANICAL ALLOYING AND COMBUSTION SYNTHESIS OF TIO2-AI-C POWDER MIXTURE
A mixture of Tio2+Al+C powders was mechanically activated using a planetary ball mill under different milling conditions wherein the milled powders were further subjected to combustion synthesis to produce TiC+Al2O3 composite. The mechanically alloyed powders were characterized by X-Ray diffraction analysis and TEM investigations. XRD analysis of milled powder mixture showed no significant reac...
متن کاملMechanically Activated Combustion Synthesis of B4C-TiB2 Nanocomposite Powder
Boron carbide is one of the hardest materials. The combustion method was used to synthesize B4C-TiB2 nanocomposite powder in a B2O3-Mg-TiO2-C system. An experimental study of the formation of B4C–TiB2 nanoparticles was conducted in the thermal explosion mode. A mixture of B2O3:TiO2:Mg:C at a molecular ratio of 3:1:12:1 was chosen to obtain the B4C–TiB2. This powder mixture was milled for differ...
متن کاملPREPARATION OF NANO-STRUCTURAL Al2O3-TiB2 IN-SITU COMPOSITE USING MECHANICALLY ACTIVATED COMBUSTION SYNTHESIS FOLLOWED BYINTENSIVE MILLING
Abstract: Nano-structural synthesized materials can be fabricated utilizing intensive milling after combustion synthesis. The Al2O3-TiB2 ceramic composite has been synthesized by aluminothermic reactions between Al, Ti (TiO2), and B (B2O3 or H3BO3). Boric acid (H3BO3) is less expensive than boron oxide, and after being dehydrated at 200°C, boron oxide will be obtained. In this study, Al, TiO2, ...
متن کامل