Effects of T2 Heat Treatment on Microstructure and Properties of the Selective Laser Melted Aluminum Alloy Samples

نویسندگان

  • Lianfeng Wang
  • Jing Sun
  • Xiaogang Zhu
  • Lingyu Cheng
  • Yun Shi
  • Lijie Guo
  • Biao Yan
چکیده

In this paper, aluminum alloy samples were fabricated by selective laser melting (SLM) and subsequently T2 heat treatment was undertaken. In order to obtain comprehensive results, various experiments on densification, hardness, tensile strength, bending strength and microstructure characterization were carried out. The results show that densification of samples after T2 heat treatment does not vary very much from the SLMed ones, while the Brinell hardness and strength decreases to about 50%. Moreover, the plasticity and fracture deflection increases about 3 fold. The effects on the microstructure and the mechanical properties of the SLMed aluminum alloy samples and subsequent T2 heat treatment were studied.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

EFFECT OF T6 HEAT TREATMENT ON MECHANICAL PROPERTIES OF CERAMIC REINFORCED CASTED ALUMINUM ALLOY

Aluminium base alloy (Al-Cu-Si) was reinforced with silicon carbide (SiC) particles, in various percentage compositions from 0-20 wt%. Silicon carbide particle size of 20µm was selected. The molten slurry of SiC reinforced base aluminium metal was casted through green and dry sand casting methods and solidification process was carried out under ambient conditions. A selected population...

متن کامل

EFFECTS OF REINFORCEMENT VOLUME FRACTION, REINFORCEMENT SIZE AND SOLUTION HEAT TREATMENT ON THE MICROSTRUCTURE OF THE TWO DIFFERENTLY PROCESSED A35&SICPCOMOSITES

In this study different volume fractions of SiC particles of various sizes were introduced into the semisolid A356 aluminum alloy by a mechanical stirrer. Then the slurry was poured into a permanent die of certain dimensions either when the metal alloy was partially solid (semisolid-semisolid or SS route) or after reheating to above the liquidus temperature of the alloy (semisolid-liquid or SL ...

متن کامل

Effects of Various Ageing Heat Treatments on Microstructural Features and Hardness of Piston Aluminum Alloy

Piston aluminum alloys have different intermetallic phases, such as Cu3Al, Mg2Si ,and AlNi phases. The morphology and the distribution of such phases have important roles on mechanical properties of the piston material. Therefore, in this research, various ageing heat treatments on the mentioned material were done and the microstructural feature and the hardness were studi...

متن کامل

The Effects of Mould Materials on Microstructure and Mechanical Properties of Cast A356 Alloy

Abstract In this study, the effects of mould materials on microstructure and mechanical properties of cast A356 Al alloy were investigated. The alloy was poured into three different moulds. Then the samples were homogenised and applied T6 heat treatment. The optical, Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) studies were made. Secondary dendrite arm spacing (SD...

متن کامل

EFFECTS OF A MODIFIED SIMA PROCESS ON THE STRUCTURE, HARDNESS AND MECHANICAL PROPERTIES OF Al-12Zn-3Mg-2.5Cu ALLOY

A modified strain-induced melt activation (SIMA) process was applied and its effect on the structural characteristics and hardness of the aluminum alloy Al–12Zn–3Mg–2.5Cu was investigated. Specimens subjected to a deformation of 40% at 300 °C were heat treated at various times (10-40 min) and temperatures (550-600 °C). Microstructural studies were carried out using opt...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 11  شماره 

صفحات  -

تاریخ انتشار 2018