Magnetism and superconductivity in La0.7Ca0.3MnO3/YBa2Cu3O7−δ superlattices

Ferromagnetic/superconducting proximity effect in La0.7Ca0.3MnO3 /YBa2Cu3O7−δ superlattices

Symmetrical interfacial reconstruction and magnetism in La0.7Ca0.3MnO3/YBa2Cu3O7/La0.7Ca0.3MnO3 heterostructures

We have analyzed the interface structure and composition of La0.7Ca0.3MnO3/YBa2Cu3O7/La0.7Ca0.3MnO3 trilayers by combined polarized neutron reflectometry, aberration-corrected microscopy, and atomic column resolution electron-energy-loss spectroscopy and x-ray absorption with polarization analysis. We find the same stacking sequence at both top and bottom cuprate interfaces. X-ray magnetic circ...

Giant magnetoresistance in ferromagnet/superconductor superlattices.

We show magnetoresistance in excess of 1000% in trilayers containing highly spin-polarized La0.7Ca0.3MnO3 and high-Tc superconducting YBa2Cu3O7. This large magnetoresistance is reminiscent of the giant magnetoresistance (GMR) in metallic superlattices but with much larger values, and originates at spin imbalance due to the injection of spin-polarized carriers. Furthermore, in contrast to ordina...

Transparent conducting oxides: A δ-doped superlattice approach

Metallic states appearing at interfaces between dissimilar insulating oxides exhibit intriguing phenomena such as superconductivity and magnetism. Despite tremendous progress in understanding their origins, very little is known about how to control the conduction pathways and the distribution of charge carriers. Using optical spectroscopic measurements and density-functional theory (DFT) simula...

ساخت نانو بلورک‌های δ-7O3Cu2YBa به روش مکانوشیمیایی و بررسی دمای گذار ترکیبات -7O3Cu2YBa(x-1) + 2 xMnO (02/0 ،015/0 ،01/0 ،005/0 ،0 = x)

In this research, YBa2Cu3O7-d (0 < d < 1) nanocrystalite superconductor was prepared by mechanochemical alloying method. We synthesized YBa2Cu3O7-d via mixing the BaCO3, Y2O3, CuO powders and milling in SPEX 8000 for 5h with weight ratio of ball to powder 10:1 and steel balls of 11mm diameter, followed by heating for 4h at 850 ˚C. The superconductor phase formation process was completed with si...