Nano-structured ZnO films by sol-gel process
نویسندگان
چکیده
Thin films of ZnO grown by sol-gel spin method using two different precursors viz. zinc nitrate and zinc acetate have been characterized for their crystalline nature and associated nanostructures. In some cases, the films consist of nanostructures in the form of nanocrystals and nanoneedles of dimensions in the range 15-60 nm. A comparison between the physical characterization and the nanostructures of the films grown by two different precursor materials has been presented and the results are discussed in terms of the fundamental considerations governing the growth kinetics of the ZnO films.
منابع مشابه
Studies on sol-gel dip-coated nanostructured ZnO thin films
Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...
متن کاملPreparation and proposed mechanism of ZnO Nanostructure Thin Film on Glass with Highest c-axis Orientation
In this paper, ZnO thin film is deposited on slide glass substrate using the sol-gel process. Presenting well-defined orientation of ZnO thin films Nanostructure were obtained by dip coating of zinc acetate dihydrate, monoethanolamine (MEA), de-ionized water and isopropanol alcohol. The annealed ZnO thin films were transparent ca 85-90% in visible range with an absorption edges at about 375 nm....
متن کاملCrystallization Kinetics of Hydroxyapatite Nano-films on Stainless Steel Through a Sol-Gel Process
This article describes the preparation and analysis of nano hydroxyapatite (HA) films on stainless steel 316L through sol-gel technique. The process started with preparation of a nitrate and phosphate sol. After aging the sol for 24 h at room temperature a SS316 substrate was dip-coated and heat-treated at 350 to 450 °C for different times in air. The coating phase and structure on subs...
متن کاملSynthesis of Zinc Oxide Nanostructured Thin Film by Sol- Gel Method and Evaluation of Gas Sensing Properties
Ethanol (C2H6O) sensitivity of zinc oxide (ZnO) thin film has been studied in present work. Semiconductor thin films of zinc oxide (ZnO) were deposited onto alkali-free glass substrates by the sol–gel method and dip-coating technique. The ZnO sol was synthesized by dissolving zinc acetate dehydrate in ethanol, and then adding Tetra ethanol-amine. The as-coated films were preheated at 150 ºC fo...
متن کاملInvestigation on the structural, morphological and photochemical properties of spin-coated TiO2 and ZnO thin films prepared by sol-gel method
In this study, TiO2 and ZnO nanofilms were prepared by sol-gel spin-coating method. Nanofilms were characterized by X-ray Diffraction (XRD), Energy Dispersive Analysis of X-ray (EDX), Scanning Electron Microscopy (SEM) and Field Emission Scanning Electron Microscopy (FE-ESM). Structural and morphological properties of nanofilms were investigated. The average crystalline size of ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2008