Optimization of dye adsorption time and film thickness for efficient ZnO dye-sensitized solar cells with high at-rest stability
نویسندگان
چکیده
Photoelectrodes for dye-sensitized solar cells were fabricated using commercially available zinc oxide (ZnO) nanoparticles and sensitized with the dye N719. This study systematically investigates the effects of two fabrication factors: the ZnO film thickness and the dye adsorption time. Results show that these two fabrication factors must be optimized simultaneously to obtain efficient ZnO/N719-based cells. Different film thicknesses require different dye adsorption times for optimal cell performance. This is because a prolonged dye adsorption time leads to a significant deterioration in cell performance. This is contrary to what is normally observed for titanium dioxide-based cells. The highest overall power conversion efficiency obtained in this study was 5.61%, which was achieved by 26-μm-thick photoelectrodes sensitized in a dye solution for 2 h. In addition, the best-performing cell demonstrated remarkable at-rest stability despite the use of a liquid electrolyte. Approximately 70% of the initial efficiency remained after more than 1 year of room-temperature storage in the dark. To better understand how dye adsorption time affects electron transport properties, this study also investigated cells based on 26-μm-thick films using electrochemical impedance spectroscopy (EIS). The EIS results show good agreement with the measured device performance parameters.
منابع مشابه
Influence of nanostructured TiO2 film thickness on photoelectrode structure and performance of flexible Dye- Sensitized Solar Cells
A commercial Ti-Nanoxide was deposited on In-doped SnO2 (ITO) polymer substrates by tape casting technique with different thicknesses (7, 14 and 36μm) to be used as photoelectrode in flexible dye-sensitized solar cells (DSSCs). Ruthenium dye was adsorbed on each TiO2 film for 24 h. The resulting photoelectrodes were used to form flexible DSSCs in combination with...
متن کاملInfluence of TiO2 layer thickness as photoanode in Dye Sensitized Solar Cells
Dye-sensitized solar cells (DSSCs) are categorized as some of inexpensive thin-film solar cells. The basis and foundation of these cells is a semiconductor that consists of an electrolyte and a light-sensitive anode. Titanium dioxide (TiO2) is a semiconductor that plays the role of anode and is the main constituent of these cells. In this paper, we have addressed the functionality and performan...
متن کاملHigh Efficient Transparent TiO2 Nanotube Dye-Sensitized Solar Cells: Adhesion of TiO2 Nanotube Membrane to FTO by Two Different Methods
In order to fabricate transparent TiO2 nanotube dye-sensitized solar cells, anodically growth nanotube membranes are detached from Ti substrate by a re-anodization method. The membranes are transferred on FTO glass by two different methods. At the first one, 100mM Ti-isopropoxide is used to make TiO2 nanoparticles for adhering TiO2 nanotube membranes to FTO and ...
متن کاملApplications of light scattering in dye-sensitized solar cells.
Light scattering is a method that has been employed in dye-sensitized solar cells for optical absorption enhancement. In conventional dye-sensitized solar cells, large TiO(2) particles with sizes comparable to the wavelength of visible light are used as scatterers by either being mixed into the nanocrystalline film to generate light scattering or forming a scattering layer on the top of the nan...
متن کاملDual-functional ZnO nanorod aggregates as scattering layer in the photoanode for dye-sensitized solar cells.
A bilayered ZnO photoanode was constructed for dye-sensitized solar cells with a high conversion efficiency of 4.0%. One layer made of ZnO nanocrystallites increases dye adsorption, and the other consisting of ZnO nanorod aggregates provides a directed electron pathway for the electron transport together with a prominent aggregation-induced light scattering.
متن کامل