Strong textured SmCo5 nanoflakes with ultrahigh coercivity prepared by multistep (three steps) surfactant-assisted ball milling
نویسندگان
چکیده
The high coercivity of 26.2 kOe for SmCo5 nanoflakes are obtained by multistep (three steps) surfactant-assisted ball milling. The magnetic properties, phase structure and morphology are studied by VSM, XRD and SEM, respectively. The results demonstrate that the three step ball-milling can keep more complete crystallinity (relatively less defects) during the process of milling compared with one step high energy ball-milling, which enhances the texture degree and coercivity. In addition, the mechanism of coercivity are also studied by the temperature dependence of demagnetization curves for aligned SmCo5 nanoflakes/resin composite, the result indicates that the magnetization reversal could be controlled by co-existed mechanisms of pinning and nucleation.
منابع مشابه
Ultrathin SmCo5 nanoflakes with high-coercivity prepared by solid particle (NaCl) and surfactant co-assisted ball milling
The ultrathin SmCo5 nanoflakes with average thickness smaller than 50 nm are prepared by a novel method of solid particle (NaCl) and surfactant co-assisted ball milling. The as-prepared nanoflakes exhibit a narrower thickness distribution of 10-50 nm and high coercivity of 23 kOe. The possible formation mechanism of nanoflakes are proposed. Temperature dependence of demagnetization curves indic...
متن کاملAnisotropic bonded magnets fabricated via surfactant-assisted ball milling and magnetic-field processing
Anisotropic bonded magnets are fabricated by surfactant-assisted ball milling in a magnetic field and magnetic field alignment of the milled chip-like nanoparticles of the Sm–Co and Nd–Fe–B materials. It is found that the application of magnetic fields during the ball milling strengthens the anisotropy of the chips and therefore improves the alignment. For SmCo5 phase-based chips, for instance,...
متن کاملSm-Co hard magnetic nanoparticles prepared by surfactant-assisted ball milling.
Hard magnetic nanoparticles based on the Sm(2)Co(17) and SmCo(5) systems have been successfully produced using a surfactant-assisted ball milling technique. A size-selection process has been developed to obtain nanoparticles of different sizes with narrow size distribution. Significant room-temperature coercivity up to 3.1 kOe has been achieved with the Sm(2)Co(17)-based nanoparticles of an ave...
متن کاملSurfactant-assisted Ball Milling: a Novel Route to Novel Materials with Controlled Nanostructure - a Review
Controlled Structure nanomaterials have played important roles in the advancement of targeted drug-delivery, gene silencing, therapeutics, catalysis, water purification and optoelectronics. These are probably because of their convenient and versatile sizes and shapes, large specific surface area, desirable surface properties, high chemical reactivity and physical affinity as well as attractive ...
متن کاملNd-Fe-B Nanoparticles through Surfactant Assisted Mechanical Milling and Alloy Design
Surfactant-assisted mechanical milling has been used to produce discrete nanoparticles of both Nd-Fe-B and Sm-Co amenable for bottom-up production of nanostructured or nanocomposite permanent magnets. However, in Nd-Fe-B the comminution of the material proceeds by transgranular fracture, which influences both the morphology of the nanoparticles and the magnetic properties. This paper utilizes a...
متن کامل