Nickel-induced morphology change of mesostructured alumina with enhanced catalytic activity for selective CO methanation.
نویسندگان
چکیده
Nickel-induced morphology change of mesostructured alumina with amorphous walls to bayerite tetrahedra when treated in water, and then to γ-alumina with worm-like mesopores topologically after it was calcined at 400 °C is reported. The catalytic activity for selective CO methanation increased significantly after this treatment.
منابع مشابه
A comparative study on the kinetics of carbon dioxide methanation over bimetallic and monometallic catalysts
In this paper, Ni/Al and La-Ni/Al catalysts were prepared with a co-impregnation method and employed in carbon dioxide methanation reaction. The catalytic results showed that the catalyst with (10wt.%) of lanthanum and (20wt.%) nickel had the highest activity at low temperatures in CO2 methanation and the La-Ni/Al catalysts changed the reaction path by lowering its activation energy and consequ...
متن کاملCatalytic reduction of SO2 with CH4 to elemental sulfur: A comparative analysis of alumina, copper-alumina and nickel-alumina catalysts
The catalytic reduction of sulfur dioxide with methane to form elemental sulfur has been studied. Al2O3, Cu-Al2O3 and Ni-Al2O3 were examined as catalysts and their performances were compared in terms of SO2 conversion and selectivity. Performance of the catalyst extremely enhanced when nickel and copper were added as promoters. The effects of temperature, SO2/CH4 molar ratio, and reaction...
متن کاملSurface Science Letters Catalytic Methanation over Single Crystal Nickel and Ruthenium: Reaction Kinetics on Different Crystal Planes and the Correlation of Surface Carbide Concentration with Reaction Rate
The kinetics of the reaction of H, and CO over single crystals of nickel ((100) and (111)) and ruthenium ((110) and (001)) have been studied as a function of pressure and Hz/CO ratio. A striking correlation has been observed between the measured surface carbide concentration and the rate of methane production while varying the Ha/CO ratio and the total pressure. This correlation is shown to be ...
متن کاملStructural and Catalytic Properties of Model Supported Nickel Catalysts
published in Aduonce ACS Abstracts, January 1, 1994. 0022-36S4/94/2098-124S%04.S0/0 nation at present. Martini2 and Goodmani3 have suggested that the activity of different crystal planes toward hydrogenolysis is responsible for the observed variations in activity with metal particle size. Single-crystal surface science studies have shown these structure-sensitive reactions to proceed more rapid...
متن کاملDeactivation of cobalt and nickel catalysts in Fischer-Tropsch synthesis and methanation
Deactivation of cobalt and nickel catalysts in Fischer-Tropsch synthesis and methanation JAVIER BARRIENTOS Akademisk avhandling som med tillstånd av KTH i Stockholm framlägges till offentlig granskning för avläggande av teknologie doktorsexamen fredagen den 23 september kl. " True wisdom comes to each of us when we realize how little we understand about life, ourselves, and the world around us....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nanoscale
دوره 7 13 شماره
صفحات -
تاریخ انتشار 2015