Microcracking in Composite Laminates: Simulation of Crack-Induced Ultrasound Attenuation
نویسندگان
چکیده
Microcracking in composite laminates is a known precursor to the growth of inter-ply delaminations and larger scale damage. Microcracking can lead to the attenuation of ultrasonic waves due to the crack-induced scattering. 3D elastodynamic finite integration technique (EFIT) has been implemented to explore the scattering of ultrasonic waves due to microcracks in anisotropic composite laminates. X-ray microfocus computed tomography data was directly input into the EFIT simulation for these purposes. The validated anisotropic 3D EFIT code is shown to be a useful tool for exploring the complex multiple-scattering which arises from extensive microcracking.
منابع مشابه
Micro-crack ultrasound scattering in anisotropic composite laminates
A computational model of ultrasound scattering by micro-cracks in fiber reinforced polymer laminates is presented, foundational to study of micro-crack induced ultrasound attenuation. A model for transmission scattering response is developed using a boundary integral formulation, and associated approximate scattering theories are discussed. Numerical results are presented demonstrating applicat...
متن کاملComputational modeling of micro-crack induced attenuation in CFRP composites
A computational study is performed to determine the contribution to ultrasound attenuation in carbon fiber reinforced polymer composite laminates of linear elastic scattering by matrix micro-cracking. Multiple scattering approximations are benchmarked against exact computational approaches. Results support linear scattering as the source of observed increased attenuation in the presence of micr...
متن کاملThe Initiation and Growth of Delaminations Induced by Matrix Microcracks in Laminated Composites
A recent variational mechanics analysis of microcracking damage in cross-ply laminates of the form [(S)/90n]s, where (S) is any orthotropic sublaminate much stiffer than [90n], has been extended to account for the presence of delaminations emanating from the tips of microcracks in the [902n]T sublaminate. The new two-dimensional stress analysis is used to calculate the total strain energy, effe...
متن کاملFracture Mechanics of Composites with Residual Stresses, Traction-loaded Cracks, and Imperfect Interfaces
By partitioning the total stresses in a damaged composite into either mechanical and residual stresses or into initial and perturbation stresses, it was possible to derive several exact results for the energy release rate due to crack growth. These general results automatically include the effects of residual stresses, traction-loaded cracks, and imperfect interfaces. By considering approximate...
متن کاملApplications of Finite Fracture Mechanics for Predicting Fracture Events in Composites
Many composites fail by fracture events, such as fiber breaks or matrix cracks, rather than by continuous crack growth. Conventional fracture mechanics deals with predicting crack growth. This paper suggests that conventional fracture mechanics can be extended to predict fracture events by using finite fracture mechanics. In finite fracture mechanics, the next fracture event is assumed to occur...
متن کامل