Sensitivity of novel silicate and borate-based glass structures on in vitro bioactivity and degradation behaviour
نویسندگان
چکیده
Three novel glass compositions, identified as NCL2 (SiO2-based), NCL4 (B2O3-based) and NCL7 (SiO2-based), along with apatite-wollastonite (AW) were processed to form sintered dense pellets, and subsequently evaluated for their in vitro bioactive potential, resulting physico-chemical properties and degradation rate. Microstructural analysis showed the carbonated hydroxyapatite (HCA) precipitate morphology following SBF testing to be composition-dependent. AW and the NCL7 formulation exhibited greater HCA precursor formation than the NCL2 and NCL4-derived pellets. Moreover, the NCL4 borate-based samples showed the highest biodegradation rate; with silicate-derived structures displaying the lowest weight loss after SBF immersion. The results of this study suggested that glass composition has significant influence on apatite-forming ability and also degradation rate, indicating the possibility to customise the properties of this class of materials towards the bone repair and regeneration process.
منابع مشابه
Sol-Gel Synthesis, in vitro Behavior, and Human Bone Marrow-Derived Mesenchymal Stem Cell Differentiation and Proliferation of Bioactive Glass 58S
Background: Bioactive glasses 58S, are silicate-based materials containing calcium and phosphate, which dissolved in body fluid and bond to the bone tissue. This type of bioactive glass is highly biocompatible and has a wide range of clinical applications. Methods: The 58S glass powders were synthesized via sol-gel methods, using tetraethyl orthosilicate, triethyl phosphate, and calcium nitrate...
متن کاملAn investigation on injectable composites fabricated by 45S5 bioactive glass and gum tragacanth: Rheological properties and in vitro behavior
The injectable composites were formulated from melt-derived 45S5 bioactive glass powder and gum tragacanth. The effect of tragacanth concentration (2 and 4 w/v%) and powder to liquid ratio (P/L= 1.5 to 2.5) on rheological properties, injectability, degradation, swelling, and bioactivity the composites was studied. With the increase of P/L ratio and tragacanth concentration, the force requ...
متن کاملIn vitro behavior of silk fibroin-coated calcium magnesium silicate scaffolds
Bioceramic scaffolds such as silicate bioceramics have been widely used for bone tissue engineering. However, their high degradation rate, low mechanical strength and surface instability are main challenges compromising their bioactivity and cytocompatibility which further negatively affect the cell growth and attachment. In this study, we have investigated the effects of silk fibroin coating o...
متن کاملIn Vitro Assessment of Laser Sintered Bioactive Glass Scaffolds with Different Pore Geometries
The pore geometry of bioactive glass scaffolds intended for use in bone repair or replacement is one of the most important parameters that could determine the rate of bone regeneration. The pore geometry would also affect the mechanical properties of the scaffolds and their rate of degradation. Scaffolds with five different architectures, having ~50% porosity, were fabricated with silicate (13–...
متن کاملBioactive Glass Fiber-Reinforced PGS Matrix Composites for Cartilage Regeneration
Poly(glycerol sebacate) (PGS) is an elastomeric polymer which is attracting increasing interest for biomedical applications, including cartilage regeneration. However, its limited mechanical properties and possible negative effects of its degradation byproducts restrict PGS for in vivo application. In this study, a novel PGS-bioactive glass fiber (F18)-reinforced composite was developed and cha...
متن کامل