OXIDATION PERFORMANCE OF V-Cr-Ti ALLOYS*
نویسنده
چکیده
The submitted manuscript has been created by the University of Chicago as Operator of Argonne National Laboratory (“Argonne”) under Contract No. W-31-109-ENG-38 with the U.S. Department of Energy. The U.S. Government retains for itself, and others acfing on its behalf, a paid-up, nonexclusive, irrevocable worldwide license in said article to reproduce, prepare derivative works, distribute copies to the public, and perform publicly and display publicly, by or on behalf of the Government.
منابع مشابه
Hydrogen Isotope Effects on Absorption Properties of Ti–Cr–V Alloys*
Ti–Cr–V alloys are known to absorb protium (hydrogen atom) up to H/M = 2, while Cr-rich alloys absorb up to H/M = 1 because of the formation of mono-protides (mono-hydrides). However, few hydrogen isotope effects of the Ti–Cr–V alloys have been reported. This paper aims to clarify the hydrogen isotope effects on the absorption properties of the Ti–Cr–V alloys in a composition range near the bou...
متن کاملThe Effects of Beryllium Additions on the Oxidation of Nickel Aluminide and Titanium Aluminide Based Intermetallics
The effects of Be additions on the oxidation behavior of ~-NiAl in moist air at 1000°C and borderline alumina-forming y (TiAI) + Laves Ti-Al-Cr based alloys at 800°C and 1000°C in dry and moist air were investigated. The addition of Be to ~-NiAl suppressed the formation of transient alumina, and resulted in the formation of a protective BeAl20 4 spinel phase. In dry air, the addition of Be to t...
متن کاملThe effect of Y and Ti on FeCrAl oxidation at 1400 C
Inco alloy MA956 (Fe-20wt%Cr-4.5%Al-0.35%Ti + 3~01% Y203-A1203) was oxidized in 1 atm of dry, flowing O2 at 1400 OC. Good scale-metal adhesion was observed. Some spalling occurred upon cooling, but it remained within the oxide, not through to the bare metal. Cyclic experiments showed good scale adherence. Y was found to segregate to the oxide grain boundaries and by implication to have modified...
متن کاملAlloying and Properties of C14–NbCr2 and A15–Nb3X (X = Al, Ge, Si, Sn) in Nb–Silicide-Based Alloys
The oxidation of Nb-silicide-based alloys is improved with Al, Cr, Ge or Sn addition(s). Depending on addition(s) and its(their) concentration(s), alloyed C14-AB₂ Laves and A15-A₃X phases can be stable in the microstructures of the alloys. In both phases, A is the transition metal(s), and B and X respectively can be Cr, Al, Ge, Si or Sn, and Al, Ge, Si or Sn. The alloying, creep and hardness of...
متن کاملNew Creep-Resistant Cast Alloys with Improved Oxidation Resistance in Water Vapor at 650–800°C
Cast stainless steel CF8C-Plus (19wt%Cr/12%Ni) has excellent creep properties, but limited oxidation resistance above 700°C in environments containing H2O. One strategy to improve the alloy oxidation performance is to increase the Cr and Ni concentration. Two new alloys, with, respectively, 21wt%Cr–15wt%Ni and 22wt%Cr–17.5wt%Ni were therefore developed and their long-term oxidation behaviors in...