MgB2 superconducting tapes with mechanically alloyed precursor powders as a possible alternative to NbTi
نویسنده
چکیده
منابع مشابه
Anisotropy of the critical current in MgB2 tapes made of high energy milled precursor powder
For applications of MgB2 wires or tapes, high critical currents in high magnetic fields are essential. By using tapes in superconducting coils the anisotropic behaviour of the critical current, i.e. the dependence on the direction of the external field in relation to the tape surface, has to be taken into account. The anisotropy of MgB2 tapes with mechanically alloyed (MA) precursor powder and ...
متن کاملپیشرفتهای اخیر در زمینه ساخت سیم و نوار ابررسانای MgB2
MgB2 wire and tape were prepared using the powder in tube and reaction in-situ technique. All samples were characterized using the XRD, SEM, TEM, as well as transport and magnetic measurements. High transport and magnetic critical current density values have been obtained for metal-clad wires and tapes. Different sheath materials have been examined, but Fe appears to be the best sheath for MgB...
متن کاملFabrication of Chemically Doped, High Upper Critical Field Magnesium Diboride Superconducting Wires
Controlled chemical doping of magnesium diboride (MgB2) has been shown to substantially improve its superconducting properties to the levels required for high field magnets, but the doping is difficult to accomplish through the usual route of solid state reaction and diffusion. Further, superconducting cables of MgB2 are difficult to fabricate because of the friable nature of the material. In t...
متن کاملEffect of ball milling on the local magnetic flux distribution and microstructure of in situ Fe/MgB2 conductors
The effects of the precursor milling energy on the superconducting and microstructural homogeneity of Fe-sheathed MgB2 monocore wires and tapes have been investigated. The conductors were produced by the powder-in-tube method using drawing and rolling deformation methods and in situ reaction. Combined magnetooptical, structural and magnetization measurements were performed on MgB2 superconducti...
متن کاملStructural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2008