Superconducting and structural properties of plasma sprayed Y-Ba-Cu-O layers deposited on metallic substrates*
نویسنده
چکیده
The properties of plasma sprayed Y-Ba-Cu-O coatings deposited on metallic substrates are studied. Stainless steel, nickel steels and pure nickel are used as substrate. Y-Ba-Cu-O deposited on stainless steel and nickel steel reacts with the substrate. This interaction can be suppressed by using an yttria-stabilized zirconia (YsZ) diffusion barrier. However, after heat treatment the Y-Ba-Cu-O layers on YsZ show cracks perpendicular to the surface. As a result the critical current density is very low. The best results are obtained for Y-Ba-Cu-O deposited on pure nickel; here no cracks perpendicular to the surface are observed. The critical current increases with the anneal temperature but annealing for longer than 10 h does not seem to improve the superconducting properties any further.
منابع مشابه
Enhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملMorphological, structural and photoresponse characterization of ZnO nanostructure films deposited on plasma etched silicon substrates
ZnO nanostructure films were deposited by radio frequency (RF) magnetron sputtering on etched silicon (100) substrates using dry Ar/SF6 plasma, at two etching times of 5 min and 30 min, and on non etched silicon surface. Energy dispersive X-ray (EDX) technique was employed to investigate the elements contents for etched substrates as well as ZnO films, where it is found to be stoichiometric. Su...
متن کاملA Study of ZnO Buffer Layer Effect on Physical Properties of ITO Thin Films Deposited on Different Substrates
The improvement of the physical properties of Indium Tin Oxide (ITO) layers is quite advantageous in photovoltaic applications. In this study the ITO film is deposited by RF sputtering onto p-type crystalline silicon (c-Si) with (100) orientation, multicrystalline silicon (mc-Si), and glass substrates coated with ZnO and annealed in vacuum furnace at 400°C. Electrical, optical, structural a...
متن کاملContributions of CuO planes and CuO chains on the transport
We have investigated the contributions of CuO planes and CuO chains on the transport properties of YBa Cu O by 2 2 4 8 Ž . Ž . measuring the electrical resistivity and thermoelectric power S of Y Pr Ba Cu Zn O , Y Ca Ba Cu O and 1yx x 2 1yy y 4 8 1yx x 2 4 8 Ž . YBa Cu Ga O . Pr reduces the mobile carrier concentration in the CuO planes in YBa Cu O , as a consequence, the 2 1yx x 4 8 2 2 4 8 Ž ...
متن کاملComposition of Pulsed-Laser-Deposited Y-Ba-Cu-O and Ba-K-Bi-O Thin Films
The composition of pulsed-laser-deposited Y-Ba-Cu-O and Ba-K-Bi-O thin films is shown to be strongly affected by target conditioning, gas pressure, and targetsubstrate distance. For both compounds, ablation from a freshly sanded target surface results in films with an excess of the more volatile elements. The concentration of these volatile elements in the films decreases until the system reach...
متن کامل