Electric field and potential around localized scatterers in thin metal films studied by scanning tunneling potentiometry

نویسندگان

  • Geetha Ramaswamy
  • A. K. Raychaudhuri
چکیده

Direct observation of electric potential and field variation near local scatterers like grain boundaries, triple points and voids in thin platinum films studied by scanning tunneling potentiometry is presented. The field is highest at a void, followed by a triple point and a grain boundary. The local field near a void can even be four orders of magnitude higher than the macroscopic field. This indicates that the void is the most likely place for an electromigration induced failure. The field build up near a scatterer strongly depends on the grain connectivity which is quantified by the average grain boundary reflection coefficient, estimated from the resistivity. ∗email: [email protected] †email: [email protected]

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Local transport properties of thin bismuth films studied by scanning tunneling potentiometry.

Charge transport in 20–30-Å-thick Bi films is studied by scanning tunneling potentiometry at room temperature. Deposition at T5140 K onto InP-based multilayer substrates leads to flat and continuous films that are subjected to a lateral current density of up to 8310 A/cm. We find that scattering at surface defects and grain boundaries gives rise to discontinuities in the local electrochemical p...

متن کامل

Scanning tunneling potentiometry (STP) studies of gold islands on a thin carbon film

The technique of scanning tunneling microscopy (STMJ has been used to study the spatial variation of the electric potential on thin film surfaces. Topography and potential distribution of the film surface are measured simultaneously. A lateral voltage gradient is obtained by applying a DC voltage bias to a metal film. With our experimental arrangement potential differences of a few @V can be di...

متن کامل

Nano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy

ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...

متن کامل

Nano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy

ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...

متن کامل

Near-field characterization of Bragg mirrors engraved in surface plasmon waveguides

Surface plasmon waveguides (SPW’s) are metal ridges featuring widths in the micrometre range and thicknesses of a few tens of nanometres. A focused ion beam (FIB) has been used to carve micro–scatterers into gold SPW’s and the near–field distributions around these micro-structures are observed by means of a Photon Scanning Tunneling Microscope (PSTM). On the basis of near-field images, we show ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 1998