Surface modification of ferritic steels using MEVVA and duoplasmatron ion sources.
نویسندگان
چکیده
Metal Vapor Vacuum Arc (MEVVA) ion source (IS) is a unique tool for production of high intensity metal ion beam that can be used for material surface modification. From the other hand, the duoplasmatron ion source provides the high intensity gas ion beams. The MEVVA and duoplasmatron IS developed in Institute for Theoretical and Experimental Physics were used for the reactor steel surface modification experiments. Response of ferritic-martensitic steel specimens on titanium and nitrogen ions implantation and consequent vacuum annealing was investigated. Increase in microhardness of near surface region of irradiated specimens was observed. Local chemical analysis shows atom mixing and redistribution in the implanted layer followed with formation of ultrafine precipitates after annealing.
منابع مشابه
Review of Negative Hydrogen Ion Sources High Brightness/high Current
Due to the development of reliable H ion sources, charge-exchange injection into circular accelerators has become routine. This paper reviews recent developments in negative hydrogen ion sources. The underlying physics, operating parameters and beam characteristics of selected sources will be described and compared. Figure 1: History of duoplasmatron and surface source development.
متن کاملRetention and release behaviors of plasma-loaded hydrogen in ferritic steels
In order to understand retention and release behaviors of plasma-loaded hydrogen in ferritic steels, hydrogen depth profiles were examined by means of a tritium imaging plate technique (TIPT). Hydrogen release was strongly affected by trapping effect in bulk and/or barrier effect of surface oxide layers during long term storage in air at room temperature (RT) and even heating in vacuum. Helium ...
متن کاملInfluence of nitrogen ion implantation on the nanostructure and corrosivity of Ni/stainless steel substrates
Ion implantation is a surface modification technology to produce new material on the surface by impingement of high energy ions from the ion accelerator. In this work, AISI 304 stainless steels were coated with 90 nm Ni film by electron beam deposition and implanted by a flow of 5×1017 N cm−2 at 400 K temperature with different implantation energies of 10, 20, 30 and 40 keV. The prepared sample...
متن کاملFTP1/01 Dynamic Mechanical Properties of Reduced Activation Ferritic Steels
A fatigue test method by a miniaturized hourglass-shaped fatigue specimen has been developed for International Fusion Materials Irradiation Facility (IFMIF) and sufficient potential as the alternative to a conventional large specimen was presented. Furthermore, focused ion beam micro-sampling method was successfully applied to microstructural analysis on fracture process. Where, the effects of ...
متن کاملWelding Research
Although solidification cracking is not usually regarded as a serious problem when welding ferritic steels, improvements in the submerged arc welding process, using higher deposition rates and faster welding speeds, have led to welding conditions more likely to give cracking. Furthermore, the need to weld stronger tougher steels, where the inspection requirements are more stringent, has led to ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- The Review of scientific instruments
دوره 87 2 شماره
صفحات -
تاریخ انتشار 2016