Fracture experiments in a high-strength ductile steel (2.3Ni-1.3Cr-0.17C) were conducted under static and dynamic loading conditions in a three-point bend and a one-point bend configurations. A qualitative description of the influence of loading rate on the microscopic features of the fracture surfaces and their role in the fracture initiation process was considered. The fracture surfaces consist of tunneled region and shear lips. The size of the shear lips increases with increasing loading rate and is characterized by microvoids and cell structures. The tunneled region consists of large voids and micro-voids that coalesce by impingement. At high loading rates, localized molten zones are observed at the tunnel-shear lip interface. @DOI: 10.1115/1.1371231#
منابع مشابه
Brazilian Test for Tensile Failure of Anisotropic Shale under Different Strain Rates at Quasi-static Loading
Shale formations show obvious anisotropic characteristics in their mechanical properties due to pronounced bedding planes and natural fractures. This anisotropic behavior generally creates complex fracturing networks and is crucial to gas shale stimulation. Although much research has been done to study the anisotropic compression behaviors of shale with static and quasi-static strain rates, the...
متن کاملEffect of Surface Roughness Morphology on Bond Strength of Thermal Sprayed WC-10Co-4Cr Ceramic/Metal Coating
In this study, the effect of surface roughness and roughness morphology on the bond strength of WC-Co-Cr coatings has investigated. The three different surfaces morphology are use for this purpose. The first and tow samples sandblasted with alumina and silicon carbide respectively. Other sample no sandblasted before spraying process. The same WC-10Co-4Cr coating deposited on the substrates with...
متن کاملEffect of Defects on Mechanical Properties of Graphene under Shear Loading Using Molecular Dynamic Simulation
Graphene sheet including single vacancy, double vacancy and Stone-Wales with armchair and zigzag structure was simulated using molecular dynamics simulation. The effect of defects on shear’s modulus, shear strength and fracture strain was investigated. Results showed that these shear properties reduce when the degrees of all kinds of defects increase. The dangling bond in SV and DV defected gr...
متن کاملImpact of High Strength Rebars on Seismic Behavior of Lightly Reinforced Boundary Elements
Considering economical reasons and attempting to reduce carbon foot print of concrete structures, there is increasing tendency toward use of high strength reinforcement in seismically active regions. ACI 318-19, Iranian steel rebars standard INSO 3132 and next edition of Iranian national building allow the use of high strength rebars in elements of ductile force resisting systems. Therefore it ...
متن کاملDamage Behavior in Modern Automotive High Strength Dual Phase Steels During Uniaxial Tensile Deformation
In the present research, damage mechanisms during room temperature uniaxial tensile testing of two different modern high strength dual phase steels,DP780 and DP980, were studied. Detailed microstructural characterization of the strained and sectioned samples was performed by scanning electron microscopy (SEM). The results revealed that interface decohesion, especially at the triple junctions of...
متن کامل