Influence of dopants and substrate material on the formation of Ga vacancies in epitaxial GaN layers
نویسندگان
چکیده
We have applied a low-energy positron beam and secondary ion mass spectrometry to study defects in homoepitaxial and heteroepitaxial GaN layers. Positron experiments reveal high concentrations of Ga vacancies in nominally undoped n-type GaN, where the conductivity is due to unintentional oxygen incorporation. Ga vacancies are observed in both homoepitaxial and heteroepitaxial layers, indicating that their formation is independent of the dislocation density. No Ga vacancies are detected in p-type or semi-insulating samples doped with Mg, as predicted by the theoretical formation energies. In samples where n-type conductivity is due to Si doping and the incorporation of oxygen impurities is suppressed, the concentration of Ga vacancies is much lower than in n-type samples containing oxygen. This indicates that the presence of oxygen donor in GaN promotes the formation of Ga vacancy. We suggest that this effect is due to the creation of VGa-ON complexes during the epitaxial growth.
منابع مشابه
CHARACTERIZATION OF NATIVE VACANCIES IN EPITAXIAL GaN AND ZnSe SEMI- CONDUCTOR LAYERS BY POSITRON ANNIHILATION SPECTROSCOPY
Point defects in epitaxial GaN and ZnSe semiconductor layers have been studied using a low-energy positron beam. Ga vacancies are found to be present in n-type GaN grown by metal organic chemical vapor deposition, where the conductivity is due to residual oxygen. When n-type silicon impurity doping is done, clearly less vacancies are observed. In Mgdoped p-type and semi-insulating materials the...
متن کاملCUBIC GaN HETEROEPITAXY ON THIN-SiC-COVERED Si(001)
We have investigated the growth conditions of cubic GaN (β-GaN) layers on very thin SiC-covered Si(001) by using gas-source molecular beam epitaxy as functions of SiC layer thickness, Ga-cell temperature and substrate temperature. Under the present SiC formation conditions on Si substrates by carbonization using C2H2 gas, the SiC layers with the thickness between 2.5 and 4 nm result in the epit...
متن کاملIMPURITY DECORATION OF NATIVE VACANCIES IN Ga AND N SUBLATTICES OF GALLIUM NITRIDE
The e ects of impurity atoms as well as various growth methods to the formation of vacancy type defects in gallium nitride (GaN) have been studied by positron annihilation spectroscopy. It is shown that vacancy defects are formed in Ga or N sublattices depending on the doping of the material. Vacancies are decorated with impurity atoms leading to the compensation of the free carriers of the sam...
متن کاملCalculated strain energy of hexagonal epitaxial thin films
Generalized formulae for the strain energy of hexagonal thin films on both hexagonal and rhombohedral substrates have been developed. These formulae require knowledge of the elastic stiffness coefficients and the lattice parameters of the film and only the lattice parameters of the substrate. Example calculations of the strain energy present in the strained film-substrate material combinations ...
متن کاملOxynitride mediated epitaxy of gallium nitride on silicon(1 1 1) substrates in a merged hydride/metal-organic vapor phase epitaxy system
A technique was developed to deposit GaN on a Si(1 1 1) substrate by a four-step process in a single reactor: formation of ultra-thin oxide, conversion to an oxynitride via NH3 exposure at the onset of growth, low-temperature MOCVD of GaN, followed by HVPE of GaN. It was found that this oxynitride compliant layer served to relieve stress at the GaN/Si interface as well as protect the Si substra...
متن کامل