Electrolyte Degradation in Anode Supported Microtubular YSZ-based Solid Oxide Steam Electrolysis Cells at high voltages of operation

Degradation of solid oxide electrolysis cells (SOECs) is probably the biggest concern in the field of high temperature steam electrolysis (HTSE). Anode supported, YSZ-based microtubular solid oxide fuel cells (SOFC) have been tested in fuel cell mode and also at high voltages (up to 2.8V) under electrolysis mode. At high steam conversion rates the cell voltage tends to saturate. Our hypothesis is that this effect is caused by the electroreduction of the thin YSZ electrolyte which induces electronic conduction losses. YSZ reduction increases the cathode activity and reduces cathode overpotential. Operation of the cell in severe electrolyte reduction conditions induces irreversible damage at the YSZ electrolyte as observed in SEM experiments by the formation of 1 Presented at Fuel Cells Science & Technology 2010, Zaragoza, Spain, 6-7 October