Tuned Magnetic Properties of L10-MnGa/Co(001) Films by Epitaxial Strain
نویسندگان
چکیده
We demonstrate that the interface structure has a significant influence on the magnetic state of MnGa/Co films consisting of L1(0)-MnGa on face-centered-cubic Co(001) surface. We reveal an antiferromagnetic to ferromagnetic magnetization reversal as a function of the lateral lattice constant. The magnetization reversal mainly originates from localized states and weak hybridization at interface due to charge redistribution between muffin-tin spheres and interstitial region. The magnetic anisotropy energy of Mn/Co interface system is enhanced with increasing in-plane lattice constant, which is ascribed to the interface interactions and the above magnetization reversal.
منابع مشابه
Correlations between morphology, crystal structure and magnetization of epitaxial cobalt-platinum films grown with pulsed laser ablation
The effects of growth rate (Gr), deposition temperature (Td), film thickness (tF ), and substrate induced strain (ǫ) on morphological, crystallographic and magnetic characteristics of equiatomic CoPt epitaxial films synthesized with pulsed laser deposition (PLD) are investigated. The (001) oriented single crystal substrates of MgO, SrTiO3 and LaAlO3 provide different degree of epitaxial strain ...
متن کاملMagnetotransport and magnetic properties of molecular-beam epitaxy L10 FePt thin films
The magnetotransport and magnetic properties of chemically ordered ~001! L10 FePt epitaxial thin films with small scale perpendicularly magnetized stripe domains have been investigated. Film growth conditions are used to systematically vary the degree of chemical order, the magnetic anisotropy, and magnetic domain sizes. The longitudinal and transverse ~Hall! resistivities are correlated with b...
متن کاملSputter-prepared (001) BiFeO3 thin films with ferromagnetic L10-FePt(001) electrode on glass substrates
Highly textured BiFeO3(001) films were formed on L10-FePt(001) bottom electrodes on glass substrates by sputtering at reduced temperature of 400°C. Good electric polarization 2Pr = 80 and 95 μC/cm2, comparable to that of the reported epitaxial films, and coercivity Ec = 415 and 435 kV/cm are achieved in the samples with 20-nm- and 30-nm-thick electrodes. The BiFeO3(001) films show different deg...
متن کاملControlling the crystallographic orientation and easy axis of magnetic anisotropy in L10 FePt films with Cu additive
By co-sputtering Cu and FePt onto Cr90Mo10 underlayers, the preferred orientation and easy axis of magnetic anisotropy of FePt films were successfully changed from the perpendicular to the in-plane direction. The pure FePt film grown on the Cr90Mo10 underlayer showed a (001) preferred orientation with out-of-plane magnetic anisotropy. As 20 and 40 vol.% Cu were doped, the FePt films showed a (2...
متن کاملReconstruction control of magnetic properties during epitaxial growth of ferromagnetic Mn3-deltaGa on Wurtzite GaN(0001).
Binary ferromagnetic Mn(3-delta)Ga (1.2<3-delta< or =1.5) crystalline thin films have been epitaxially grown on wurtzite GaN(0001) surfaces using rf N-plasma molecular beam epitaxy. The film structure is face-centered tetragonal with CuAu type-I (L1(0)) ordering with (111) orientation. The in-plane epitaxial relationship to GaN is nearly ideal with [110](MnGa) parallel[1100](GaN) and [112](MnGa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 6 شماره
صفحات -
تاریخ انتشار 2016