Date of revision: Saturday, July 21, 2001 Structural aspects of the fivefold quasicrystalline Al-Cu-Fe surface from STM and dynamical LEED studies
نویسندگان
چکیده
We investigate the atomic structure of the fivefold surface of an icosahedral AlCu-Fe alloy, using scanning tunneling microscopy (STM) imaging and a special dynamical low energy-electron diffraction (LEED) method. STM indicates that the step heights adopt (primarily) two values in the ratio of tau, but the spatial distribution of these two values does not follow a Fibonacci sequence, thus breaking the ideal bulk-like quasicrystalline layer stacking order perpendicular to the surface. The appearance of screw dislocations in the STM images is another indication of imperfect quasicrystallinity. On the other hand, the LEED analysis, which was successfully applied to Al-Pd-Mn in a previous study, is equally successful for Al-Cu-Fe. Similar structural features are found for both materials, in particular for interlayer relaxations and surface terminations. Although there is no structural periodicity, there are clear atomic planes in the bulk of the quasicrystal, some of which can be grouped in recurring patterns. The surface tends to form between these grouped layers in both alloys. For Al-Cu-Fe, the step heights measured by STM are consistent with the thicknesses of the grouped layers favored in LEED. These results suggest that the fivefold Al-Cu-Fe surface exhibits a quasicrystalline layering structure, but with stacking defects.
منابع مشابه
Real-space observation of quasicrystalline Sn monolayer formed on the fivefold surface of icosahedral AlîŠ ̧CuîŠ ̧Fe quasicrystal
We investigate a thin Sn film grown at elevated temperatures on the fivefold surface of an icosahedral AlCuFe quasicrystal by scanning tunneling microscopy (STM). At about one monolayer coverage, the deposited Sn is found to form a smooth film of height consistent with one-half of the lattice constant of the bulk Sn. Analysis based on the Fourier transform and autocorrelation function derived...
متن کاملFivefold surface of quasicrystalline AlPdMn: Structure determination using low-energy-electron diffraction
The atomic structure of the fivefold symmetric quasicrystal surface of icosahedral AlPdMn has been investigated by means of a dynamical low-energy-electron diffraction (LEED) analysis. Approximations were developed to make the structure of an aperiodic, quasicrystalline surface region accessible to LEED theory. A mix of several closely similar, relaxed, bulklike lattice terminations is favored,...
متن کاملLaser processing and microstructure of Al-Cu-Fe quasicrystalline coatings on Al-base materials
There is a large interest in using high power lasers for surface alloying or cladding on aluminium alloys, in order to enhance hardness and to improve wear resistance. A partly quasicrystalline surface layer (QC) (Al-Cu-Fe coating) has been obtained by laser cladding on Al-base materials. In addition to crystalline phases (Al5Fe2 and AlisFe4t -with dissolved copper), a quasicrystalline Al-Cu-Fe...
متن کاملCopper adsorption on the fivefold Al70Pd21Mn9 quasicrystal surface
Recently we reported the formation of a quasiperiodic Cu thin film on the fivefold icosahedral Al-Pd-Mn quasicrystal using scanning tunneling microscopy, low energy electron diffraction, and Auger electron spectroscopy. Here we provide details pertaining to the growth, stability, and structure of this film. Structural information has been gained by LEED measurements carried out at 85 K. Cu atom...
متن کاملBulk electronic structure of quasicrystals.
We use hard x-ray photoemission to resolve a controversial issue regarding the mechanism for the formation of quasicrystalline solids, i.e., the existence of a pseudogap at the Fermi level. Our data from icosahedral fivefold Al-Pd-Mn and Al-Cu-Fe quasicrystals demonstrate the presence of a pseudogap, which is not observed in surface sensitive low energy photoemission because the spectrum is aff...