Hydrothermal synthesis, off-axis electron holography and magnetic properties of Fe3O4 nanoparticles
نویسندگان
چکیده
The hydrothermal synthesis of Fe3O4 nanoparticles (NPs) (< 50 nm) from mixed FeCl3 / FeCl2 precursor solution at pH ~ 12 has been confirmed using complementary characterisation techniques of transmission electron microscopy and X-ray diffractometry. Offaxis electron holography allowed for visualisation of their single domain (SD) nature, as well as inter-particle interactions, with the latter attributed to explain the pseudo-SD/multi-domain behaviour demonstrated by bulk magnetic measurements.
منابع مشابه
Hydrothermal Synthesis of Fe3O4 Nanoparticles and Flame Resistance Magnetic Poly styrene Nanocomposite
Fe3O4 nanostructures were synthesized via a facile hydrothermal reaction. The effect of various surfactants such as cationic and anionic on the morphology of the product was investigated. Magnetic nanoparticles were added to poly styrene for preparation of magnetic nanocomposite. Nanostructures were then characterized using X-ray diffraction, scanning electron microscopy and Fourier transform i...
متن کاملGreen Synthesis of Iron Oxide-Palladium Nanocomposites by Pepper extract and Its Application in Removing of Colored Pollutants from Water
Fe3O4 nanoparticles were synthesized in the presence of pepper extract as a capping agent via a hydrothermal method. Then palladium nanoparticles and Fe3O4-Pd nanocomposites were synthesized with the aid of pepper extract as a reducing agent. Vibrating Sample magnetometer illustrated that Fe3O4 nanoparticles have super paramagnetic behaviour. The photo catalytic behaviour of Fe3O4-Pd nanocompos...
متن کاملLarge-scale synthesis of single-crystalline iron oxide magnetic nanorings.
We present an innovative approach to the production of single-crystal iron oxide nanorings employing a solution-based route. Single-crystal hematite (alpha-Fe2O3) nanorings were synthesized using a double anion-assisted hydrothermal method (involving phosphate and sulfate ions), which can be divided into two stages: (1) formation of capsule-shaped alpha-Fe2O3 nanoparticles and (2) preferential ...
متن کاملHydrothermal synthesis of cobalt oxide nanoparticles: Its optical and magnetic properties
Cobalt oxide (Co3O4) nanoparticleshave been synthesized by hydrothermal method using mixture of cobalt(II)chloride, Triton X-100 and KOH in an autoclave at 180 °C for 6 h followed by heating at 400 ºC for 3 h in air. The product have been characterized by Fourier transform infrared (FT-IR), UV-Vis spectroscopy, powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission ...
متن کاملObservation of thermally-induced magnetic relaxation in a magnetite grain using off-axis electron holography
A synthetic basalt comprising magnetic Fe3O4 grains (~ 50 nm to ~ 500 nm in diameter) is investigated using a range of complementary nano-characterisation techniques. Off-axis electron holography combined with in situ heating allowed for the visualisation of the thermally-induced magnetic relaxation of an Fe3O4 grain (~ 300 nm) from an irregular domain state into a vortex state at 550 ̊C, just b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2013