Ultrasonic Detection and Measuring of Isolated or Pitting Corrosion (ipc)
نویسنده
چکیده
AS2542.3 (Determination of Thickness – Use of Ultrasonic Testing) states: “This standard specifies six methods for determination of thickness of material based on the use of ultrasonic pulse-echo principals where the scanning and reflecting surfaces are substantially parallel”. In many cases, the principals and procedures used in AS2452.3 are not applicable for the detection and measuring of isolated or pitting corrosion, as the reflecting surfaces are not generally parallel.
منابع مشابه
Effect of Ultrasonic Nano-Crystal Surface Modification (UNSM) on the Passivation Behavior of Aged 316L Stainless Steel
Stainless steels have good corrosion resistance in many environments but welding or aging can decrease their resistance. This work focused on the effect of aging time and ultrasonic nano-crystal surface modification on the passivation behavior of 316L stainless steel. In the case of slightly sensitized 316L stainless steel, increasing the aging time drastically decreased the pitting potential, ...
متن کاملIn-Situ Observation and Acoustic Emission Analysis for Corrosion Pitting of MgCl2 Droplet in SUS304 Stainless Steel
Acoustic emission with near-field detection and optical video microscope monitoring was proposed to investigate the pitting corrosion caused by a small magnesium-chloride droplet. Four types of the detected waveforms were characterized by the wavelet analysis to investigate the corrosion of work-hardened SUS304 stainless steel. After high-activity AE signals observed, the corrosion product shee...
متن کاملNumerical Simulation of Monitoring Corrosion in Reinforced Concrete Based on Ultrasonic Guided Waves
Numerical simulation based on finite element method is conducted to predict the location of pitting corrosion in reinforced concrete. Simulation results show that it is feasible to predict corrosion monitoring based on ultrasonic guided wave in reinforced concrete, and wavelet analysis can be used for the extremely weak signal of guided waves due to energy leaking into concrete. The characteris...
متن کاملThe Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملMonitoring of corrosion damage using high-frequency guided ultrasonic waves
Due to adverse environmental conditions corrosion can develop during the life cycle of industrial structures, e.g., offshore oil platforms, ships, and desalination plants. Both pitting corrosion and generalized corrosion leading to wall thickness loss can cause the degradation of the integrity and load bearing capacity of the structure. Structural health monitoring of corrosion damage in diffic...
متن کامل