Luminescence and Fluorescence Line Narrowing Studies of Chromium Doped Glass
نویسندگان
چکیده
The technique of fluorescence l ine narrowing i s applied t o the TE 4A2 transition on Cr3+ ions in ED-2 glass. The resultant sharp zero-phonon l ine is accompanied by a vibrational sideband which carries information about the range of vibrational modes of the glass. The homogeneous broadening of the zero-phonon l ine is measured as a function of temperature.
منابع مشابه
Luminescence Properties of Oxyfluoride Glass and Glass Ceramic Doped with Y3 + Ions
Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...
متن کاملEnhanced luminescence of Er+3-doped Zinc-Lead-Phosphate Glass embedded SnO2 nanoparticles
Introduction of the nanoparticles in the bulk glass received a large interest due to their versatile application. The composition of Er+3-doped Zinc-Lead-Phosphate glass samples are prepared by melt-quenching technique. The structural and optical properties of phosphate glass have been examined by x-ray diffraction, fie...
متن کاملLuminescence Enhancement in Eu(III)-Doped Tellurite Glass Embedded Silver Nanoparticles
Introduction of the metallic nanoparticles (NPs) in the bulk glass received a large interest due to their versatile applications. The effect of silver NPs on optical properties of the Eu3+-doped zinc tellurite glasses is presented for the first time. Glass samples are prepared by melt-quenching technique. The surface plasmon absorption bands of silver NPs are recorded in the visible ...
متن کاملLuminescence Properties of TeO2-LiF-Gd2O3 Glasses
In this work, the structural properties and spectroscopic behavior 80 mol.%TeO2-20mol.%LiF glasses which were doped with 0. 05, 0. 2 mole% Gd2O3 have been studied. It was shown that, by increasing the amount of Gd2O3 the glass stability was decreased. The PL emissions at 431nm and 627nm wavelengths were distinguished by 320nm excitation. The FT-IR analysis showed deformed TeO4 groups in these ...
متن کاملتهیه و مطالعه شیشه های ﺳﺪﻳﻢ تترابورات دوپه شده با اکسید تربیوم
Terbium oxide doped tetraborate glasses were prepared from the reaction of Tb2O3 and Na2B4O7 .10 H2O on reagent grade. At first, the base borate glass of Na2B4O7 was prepared by melting dehydrated borax at 1000 ˚C for 30 min and then the obtained base glass was crushed and powdered. Appropriate amounts of Tb2O3 (5-20 mol %) and Na2B4O7 powdered glass were mixed and melted at 1200 ˚C for 15 min....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2017