Modification of Hydroxyapatite with Ion-Selective Complexants: 1-Hydroxyethane-1,1-diphosphonic Acid

نویسندگان

  • Yasmine Daniels
  • Nathalie Lyczko
  • Ange Nzihou
  • Spiro D. Alexandratos
چکیده

Hydroxyapatite (HAP) was modified with 1-hydroxyethane-1,1-diphosphonic acid (HEDP), and its effect on divalent metal ion binding was determined. HAP was synthesized from calcium hydroxide and phosphoric acid. After calcination, it was modified with HEDP, and the influence of time and temperature on the modification was investigated. HEDP incorporation increased as its initial solution concentration increased from 0.01 to 0.50 M. Unmodified and modified HAP were characterized using Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, and specific surface area analysis. Ca/P ratios, acid capacities, and phosphorus elemental analyses gave the effect of modification on composition and surface characteristics. A high reaction temperature produced new phosphonate bands at 993, 1082, and 1144 cm-1 that indicated the presence of HEDP. HAP modification at a high temperature-long reaction time had the highest HEDP loading and gave the sharpest XRD peaks. The emergence of new HAP-HEDP strands was observed in SEM images for treated samples while EDS showed high phosphorus contents in these strands. Modified HAP had a high acid capacity from the additional P-OH groups in HEDP. The P(O)OH groups maintain their ability to bind metal ions within the HAP matrix: contacting the modified HAP with 10-4 N nitrate solutions of five transition metal ions gives an affinity sequence of Pb(II) > Cd(II) > Zn(II) > Ni(II) > Cu(II). This result is comparable to that of commercially available di(2-ethylhexyl)phosphoric acid, a common solvent extractant, and the trend is consistent with the Misono softness parameter of metal ion polarizabilities.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

New amino bisphosphonate compound for skeletal imaging: Comparison study with methylenediphosphonic acid (MDP) and (1-hydroxyethane-1,1-diyl) diphosphonic acid (HEDP)

Technetium-99m radiopharmaceuticals play an important role in wide range of applications in nuclear medicine. Bone imaging agents are among the fi rst developed 99mTc-radiopharmaceuticals and the most widely used radiopharmaceuticals in diagnostic nuclear medicine [1]. Bisphosphonates (BPs) are synthetic organic compounds characterized by a P-C-P backbone structure. They are chemically stable a...

متن کامل

Cage clusters built from uranyl ions bridged through peroxo and 1-hydroxyethane-1,1-diphosphonic acid ligands.

The family of cage clusters built by uranyl ions bridged through bidentate peroxide groups has been expanded by incorporation of 1-hydroxyethane-1,1-diphosphonic (etidronic) acid ligands. Six cage clusters containing from 16 to 64 uranyl ions, as well as from eight to 32 etidronic acid ligands have been synthesized and characterized. Incorporation of etidronic acid ligands introduces both new c...

متن کامل

Behavior of Uranium(VI) during HEDPA Leaching for Aluminum Dissolution in Tank Waste Sludges

Batch adsorption/dissolution experiments were conducted to examine the interactions between U(VI) and a synthetic aluminum oxyhydroxide (boehmite, γ-AlOOH) in 1.0M NaCl suspensions containing 1-hydroxyethane-1,1-diphosphonic acid (HEDPA). In the pH range 4 to 9, complexation of Al(III) by HEDPA significantly enhanced dissolution of boehmite. This phenomenon was especially pronounced in the neut...

متن کامل

The role of 1-hydroxyethane –1, 1-diphosphonic acid on corrosion inhibition performance of calcium gluconate in mild steel

The corrosion rate of mild steel in low corrosive tap water in the absence and presence of 1hydroxy ethane-1, 1-diphosphonic acid (HEDP) and calcium gluconate have been evaluated by weight loss, electrochemical polarization and AC impedance measurements. Presence of calcium gluconate considerably enhanced the corrosion inhibition efficiency of the widely used water treatment agent HEDP. At high...

متن کامل

The effects of diphosphonates on the growth and glycolysis of connective-tissue cells in culture.

1. The effects of two diphosphonates (compounds containing a P-C-P bond), disodium dichloromethanediphosphonate and disodium 1-hydroxyethane-1,1-diphosphonate, on the metabolism of cultured rat calvaria cells, rabbit ear cartilage cells and rat skin fibroblasts were investigated. 2. The diphosphonates had no effect on the growth of cartilage cells and on the exponential growth of the calvaria c...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 54  شماره 

صفحات  -

تاریخ انتشار 2015