Synthesis and characterization of fluorinated copolyetherimides with -CH2-C6F13 side chains based on the ULTEM structure

Step polymerization of Bisphenol-A diphthalic anhydride (BAPA) with various mixtures from m-phenylene diamine (m-PDA) and 2-(perfluorohexylmethyl)butan-1,4-diamine (TFD) led to hydrophobic copolyetherimides bearing RF = -CH2-C6F13 side chains that were characterized by NMR, elementary analysis, DSC, TGA and surface energy analysis. By increasing the TFD unit %, the glass transition temperature (Tg) decreases according to the Fox equation from 217 °C (m-PDA 100 % and TFD 0% like in ULTEM 1000) to 113 °C (m-PDA 0% and TFD 100 %). Similarly the surface energy (γs) decreases from 45.3 mJ m to 27.4 mJ m. The thermal decomposition temperature (Td for 5% weight loss under argon) is slightly affected by introducing TFD units compared with Td for ULTEM and it is close to 400 °C. The best compromise between thermal stability, hydrophobic and organophilic properties as well as the ability to form a soft non-porous film by the cast-evaporating method led us to select the copolyetherimide with m-PDA 25% and TFD 75% for which Tg = 121 °C, Td = 400 °C and γs = 30.8 mJ m.