Behavior of zinc from spent zinc-carbon batteries by selective leaching with sodium hydroxide

Physical methods such as crushing and sieving followed by magnetic separation steps were applied to separate non-magnetic material (88.4 wt%) from zinc-carbon spent batteries. The oversize material was processed by eddy current separation to recover zinc sheet, carbon rods, and plastics. The undersize fraction (-2.36 mm) with a metal composition of 15.5% Zn, 17.5% Mn, and 1.4% Fe was used for the leaching experiments under different conditions such as concentration of sodium hydroxide, temperature, agitation speed, and pulp density. Selective leaching using 4 mol dm NaOH at 100 g dm solid/liquid ratio, 80C and 200 rpm gave a zinc extraction of 82% and a manganese extraction of less than 0.1%. An overall zinc recovery was about 88.5% by the processes described in this study.