Effect of Curing Rate on the Microstructure and Macroscopic Properties of Epoxy Fiberglass Composites
Curing rates of an epoxy amine system were varied via different curing cycles, and glass-fiber epoxy composites were prepared using the same protocol, with the aim of investigating the correlation between microstructure and composite properties. It was found that the fast curing cycle resulted in a non-homogenous network, with a larger percentage of a softer phase. Homogenized composite propert...
متن کاملEffect of thermal aging and fatigue on failure resistance of aerospace composite materials
Exposing a laminate structure to thermal cycles and to temperatures close to the curing temperature, followed by mechanical fatigue, cause interlaminar and intralaminar cracks leading to degradation of the mechanical properties. The effect of thermal and mechanical fatigue, as well as thermal aging, on carbon fiber composite laminate structures is under study in the present paper.
متن کاملAdhesive bonding of composites
provision of large, stress-bearing area excellent fatigue strength good shock absorption reduced galvanic corrosion no need to have access to far-side of adherend to make joint bonding is possible on dissimilar materials provision of smooth contours and sections around joint areas sealing improved damping which increases structural stiffness reduction in distortion and metal...
متن کاملAnalysis Of Vacuum Failures During Curing Of
Carbon fiber reinforced Composite structures posses‟ high strength and stiffness to weight ratios, also exhibits good fatigue resistance, and are less prone to deterioration caused by corrosion and cracking. Fabrication of these composite structures is highly process dependent. During curing process, the physical, mechanical and chemical properties are imparted to the components, and are genera...
متن کاملThe effect of Acetobacter sp. and a sulfate-reducing bacterial consortium from ethanol fuel environments on fatigue crack propagation in pipeline and storage tank steels
This paper evaluates the effects of microbiologically influenced corrosion (MIC) on fatigue-crack growth of candidate materials useful in expanding bio-ethanol usage, including a storage-tank steel (ASTM A36) and two pipeline steels (API 5L X52 and X70). The microbiological species sampled and cultivated from an ethanol fuel production stream are responsible for both acetic acid and hydrogen su...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Science translational medicine
دوره 5 200 شماره
صفحات -
تاریخ انتشار 2013