Highly (001)-oriented Ni-doped L10 FePt films and their magnetic properties
نویسندگان
چکیده
منابع مشابه
Controlling the crystallographic orientation and easy axis of magnetic anisotropy in L10 FePt films with Cu additive
By co-sputtering Cu and FePt onto Cr90Mo10 underlayers, the preferred orientation and easy axis of magnetic anisotropy of FePt films were successfully changed from the perpendicular to the in-plane direction. The pure FePt film grown on the Cr90Mo10 underlayer showed a (001) preferred orientation with out-of-plane magnetic anisotropy. As 20 and 40 vol.% Cu were doped, the FePt films showed a (2...
متن کاملEdge-modulated perpendicular magnetic anisotropy in [Co/Pd]n and L10- FePt thin film wires
Thickness modulation at the edges of nanostructured magnetic thin films is shown to have important effects on their perpendicular magnetic anisotropy. Thin film wires with tapered edges were made from [Co/Pd]20 multilayers or L10-FePt films using liftoff with a double-layer resist. The effect of edge taper on the reversal process was studied using magnetic force microscopy (MFM) and micromagnet...
متن کاملFine control of L10 ordering and grain growth kinetics by C doping in FePt films
We present the results on highly anisotropic oriented face-centered-tetragonal ordered equiatomic FePt thin films embedded in a C matrix prepared by cosputtering technique on MgO ~100! substrates at 400 °C. We have found that doping of C in FePt alloy films is an effective and appropriate way to control the L10 ordering and growth of grain size down to 4 nm. Room-temperature magnetic measuremen...
متن کاملMagnetotransport and magnetic properties of molecular-beam epitaxy L10 FePt thin films
The magnetotransport and magnetic properties of chemically ordered ~001! L10 FePt epitaxial thin films with small scale perpendicularly magnetized stripe domains have been investigated. Film growth conditions are used to systematically vary the degree of chemical order, the magnetic anisotropy, and magnetic domain sizes. The longitudinal and transverse ~Hall! resistivities are correlated with b...
متن کاملOrientation of FePt nanoparticles on top of a-SiO2/Si(001), MgO(001) and sapphire(0001): effect of thermal treatments and influence of substrate and particle size
Texture formation and epitaxy of thin metal films and oriented growth of nanoparticles (NPs) on single crystal supports are of general interest for improved physical and chemical properties especially of anisotropic materials. In the case of FePt, the main focus lies on its highly anisotropic magnetic behavior and its catalytic activity, both due to the chemically ordered face-centered tetragon...