Novel hierarchical Cd4SiS6/SiO2 based heterostructure nanowire arrays were fabricated on silicon substrates by a one-step thermal evaporation of CdS powder. The as-grown products were characterized using scanning electron microscopy, X-ray diffraction, and transmission electron microscopy. Studies reveal that a typical hierarchical Cd4SiS6/SiO2 heterostructure nanowire is composed of a single crystalline Cd4SiS6 nanowire core sheathed with amorphous SiO2 sheath. Furthermore, secondary nanostructures of SiO2 nanowires are highly dense grown on the primary Cd4SiS6 core-SiO2 sheath nanowires and formed hierarchical Cd4SiS6/SiO2 based heterostructure nanowire arrays which stand vertically on silicon substrates. The possible growth mechanism of hierarchical Cd4SiS6/SiO2 heterostructure nanowire arrays is proposed. The optical properties of hierarchical Cd4SiS6/SiO2 heterostructure nanowire arrays are investigated using Raman and Photoluminescence spectroscopy.
منابع مشابه
Hierarchical Cd4SiS6/SiO2 Heterostructure Nanowire Arrays
Novel hierarchical Cd4SiS6/SiO2 based heterostructure nanowire arrays were fabricated on silicon substrates by a one-step thermal evaporation of CdS powder. The as-grown products were characterized using scanning electron microscopy, X-ray diffraction, and transmission electron microscopy. Studies reveal that a typical hierarchical Cd4SiS6/SiO2 heterostructure nanowire is composed of a single c...
متن کاملSi/InGaN core/shell hierarchical nanowire arrays and their photoelectrochemical properties.
Three-dimensional hierarchical nanostructures were synthesized by the halide chemical vapor deposition of InGaN nanowires on Si wire arrays. Single phase InGaN nanowires grew vertically on the sidewalls of Si wires and acted as a high surface area photoanode for solar water splitting. Electrochemical measurements showed that the photocurrent density with hierarchical Si/InGaN nanowire arrays in...
متن کاملA top-down approach to fabrication of high quality vertical heterostructure nanowire arrays.
We demonstrate a novel top-down approach for fabricating nanowires with unprecedented complexity and optical quality by taking advantage of a nanoscale self-masking effect. We realized vertical arrays of nanowires of 20-40 nm in diameter with 16 segments of complex longitudinal InGaAsP/InP structures. The unprecedented high quality of etched wires is evidenced by the narrowest photoluminescence...
متن کاملOptical properties of crystalline-amorphous core-shell silicon nanowires.
The optical absorption in a nanowire heterostructure consisting of a crystalline silicon core surrounded by a conformal shell of amorphous silicon is studied. We show that they exhibit extremely high absorption of 95% at short wavelengths (λ < 550 nm) and a concomitant very low absorption of down to less than 2% at long wavelengths (λ > 780 nm). These results indicate that our nanowires do not ...
متن کاملSelf-catalyzed ternary core-shell GaAsP nanowire arrays grown on patterned Si substrates by molecular beam epitaxy.
The growth of self-catalyzed ternary core-shell GaAsP nanowire (NW) arrays on SiO2 patterned Si(111) substrates has been demonstrated by using solid-source molecular beam epitaxy. A high-temperature deoxidization step up to ∼ 900 °C prior to NW growth was used to remove the native oxide and/or SiO2 residue from the patterned holes. To initiate the growth of GaAsP NW arrays, the Ga predeposition...
متن کامل