We report a systematic study of room-temperature ferromagnetism (RTFM) in pristine MgO thin films in their amorphous and nano-crystalline states. The as deposited dc-sputtered films of pristine MgO on Si substrates using a metallic Mg target in an O₂ containing working gas atmosphere of (N₂ + O₂) are found to be X-ray amorphous. All these films obtained with oxygen partial pressure (PO₂) ~10% to 80% while maintaining the same total pressure of the working gas are found to be ferromagnetic at room temperature. The room temperature saturation magnetization (MS) value of 2.68 emu/cm³ obtained for the MgO film deposited in PO₂ of 10% increases to 9.62 emu/cm³ for film deposited at PO₂ of 40%. However, the MS values decrease steadily for further increase of oxygen partial pressure during deposition. On thermal annealing at temperatures in the range 600 to 800 °C, the films become nanocrystalline and as the crystallite size grows with longer annealing times and higher temperature, MS decreases. Our study clearly points out that it is possible to tailor the magnetic properties of thin films of MgO. The room temperature ferromagnetism in MgO films is attributed to the presence of Mg cation vacancies.
منابع مشابه
Physical Properties of Reactively Sputter-Deposited C-N Thin Films
This work aims to prepare and study amorphous carbon nitride (CNx) films. Films were deposited by reactive magnetron radiofrequency (RF) sputtering from graphite target in argon and nitrogen mixture discharge at room temperature. The ratio of the gas flow rate was varied from 0.1 to 1. Deposited films were found to be amorphous. Highest Nitrogen concentration achieved was 42 atomic percent whic...
متن کاملA study on the dependence of DC electrical properties and nanostructure of Cu thin films on film thickness
This paper reports the correlation between film thickness, nanostructure and DC electrical properties of copper thin films deposited by PVD method on glass substrate. X-ray diffraction (XRD) and atomic force microscopy (AFM) were used for crystallography and morphology investigation, respectively. Resistivity was measured by four point probe instrument, while a Hall effects measurement system w...
متن کاملA study on the dependence of DC electrical properties and nanostructure of Cu thin films on film thickness
This paper reports the correlation between film thickness, nanostructure and DC electrical properties of copper thin films deposited by PVD method on glass substrate. X-ray diffraction (XRD) and atomic force microscopy (AFM) were used for crystallography and morphology investigation, respectively. Resistivity was measured by four point probe instrument, while a Hall effects measurement system w...
متن کاملCharacterization of amorphous and nanocomposite Nb–Si–C thin films deposited by DC magnetron sputtering
متن کامل
Sputtring av Ti-Si-C-Ag-beläggningar från sammansatta sputterkällor
Abstract Today gold is used as contact material on electric contacts for low current applications. Gold, however, has low wear resistance, is expensive and environmentally stressful to produce. An alternative contact material to gold is nano composite Ti-Si-C-Ag deposited with DC-magnetron sputtering. Nano composite Ti-Si-C-Ag has so far been deposited by a compound Ti-Si-C sputter target with ...
متن کامل