Effect of grain disorientation on early fatigue crack propagation in FCC poly-crystals: a three dimensional dislocation dynamics investigation
نویسندگان
چکیده
Three-dimensional dislocation dynamics simulations are used to study micro-crack interaction with the first micro-structural barrier in face-centred cubic bi-crystals loaded in high cycle fatigue conditions. In the examined configuration, we assumed that micro-crack transmission occurs due to surface relief growth in the secondary grain ahead of the primary crack. This indirect transmission mechanism is shown to strongly depend on grain-1/grain-2 disorientation. For instance, small grain disorientation induces plastic strain localisation ahead of the crack and faster transmission through the first barrier. Conversely, large grain-1/grain-2 disorientation induces plastic strain spreading similar to crack tip blunting yielding slower indirect transmission. A semi-analytical micro-model is developed based on the present simulation results and complementary experimental observations highlighting the original
منابع مشابه
Fatigue crack growth characteristics of Fe and Ni under cyclic loading using a quasi-continuum method
A quasi-continuum (QC) method based on the embedded atom method (EAM) potential was employed to investigate the fatigue crack growth and expansion characteristics of single-crystal Fe and Ni under cyclic loading modes I and II. In particular, the crack growth and expansion characteristics of Fe and Ni under cyclic loading were evaluated in terms of atomic stress fields and force–distance curves...
متن کاملEffect of Grain Size on Collective Damage of Short Cracks and Fatigue Life Estimation for a Stainless Steel
In the short crack regime of the fatigue process, grain boundaries in steels are barriers against crack growth. In this paper, we use: (1) a method involving crack density; and (2) a method of dimensional analysis, to evaluate the effects of grain size and grain-boundary resistance on short crack behaviour and fatigue life. The results show that the fatigue life increases with a decrease in gra...
متن کاملDynamics of Nanoscale Grain-Boundary Decohesion in Aluminum by Molecular-Dynamics Simulation
The dynamics and energetics of intergranular crack growth along a flat grain boundary in aluminum is studied by a molecular-dynamics simulation model for crack propagation under steady-state conditions. Using the ability of the molecular-dynamics simulation to identify atoms involved in different atomistic mechanisms, it was possible to identify the energy contribution of different processes ta...
متن کاملAn atomistic investigation into the nature of near threshold fatigue crack growth in aluminum alloys
Despite decades of study, the atomic-scale mechanisms of fatigue crack growth remain elusive. Here we use the coupled atomistic–discrete dislocation method, a multiscale simulation method, to examine the influence of dislocation glide resistance on near-threshold fatigue crack growth in an aluminum alloy. The simulations indicate that the threshold increases with an increase in dislocation glid...
متن کاملFatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire
Fatigue properties and cracking behavior of cold-drawn commercially pure aluminum wires (CPAWs) widely used as the overhead transmission conductors were investigated. It was found that the fracture surface of the CPAWs shows an obvious four-stage fracture characteristic, i.e., crack initiation, planar crack propagation, 45°-inclined crack propagation and final rapid fracture. The crack growth m...
متن کامل