Temperature dependence of the training effect in electrodeposited Co/CoO nanotubes
نویسندگان
چکیده
High aspect ratio Co/CoO nanotubes (NTs) were obtained by potentiostatic electrodeposition of Co inside nanoporous alumina templates followed by the natural oxidation of their inner walls. Magnetic measurements performed at low temperatures after field cooling the samples from above its blocking temperature (TB 220 K), evidenced the existence of exchange bias (EB) coupling between the Co ferromagnetic outer wall and the CoO antiferromagnetic inner wall of the NTs. A decrease in the magnitude of the EB field was measured at T < TB when cycling the Co/CoO NT arrays through consecutive hysteresis loops. This decrease is known as the training effect (TE) and is here studied in the 6 K T < TB temperature range. The TE was fitted using the recursive Binek formula, giving small values for the characteristic decay rate of the training behavior, and evidencing a decrease of EB with increasing antiferromagnetic layer thickness. A phenomenological theory for the temperature dependence of the TE in exchange biased systems was applied for the first time to core-shell nanotubular structures. The good agreement obtained between the experimental results and the theoretical data, provided a strong confirmation of the qualitative correctness of the spin configuration relaxation model used in these systems. VC 2013 AIP Publishing LLC. [http://dx.doi.org/10.1063/1.4816696]
منابع مشابه
Preparation of a Novel Super Active Fischer-Tropsch Cobalt Catalyst Supported on Carbon Nanotubes
The potential of carbon nanotubes (CNT) supported cobalt catalysts for Fischer-Tropsch (FT) reaction is shown. Using the wet impregnation method cobalt on carbon nanotubes catalysts were prepared with cobalt loading varying from 15 to 45 wt. %. The catalysts are characterized by different methods including: BET physisorption, X-ray diffraction, hydrogen chemisorption, and temperature-progra...
متن کاملDomain state model for exchange bias . II . Experiments
The exchange bias coupling at ferro-/antiferromagnetic interfaces of epitaxially grown Co/CoO bilayers can be intentionally enhanced and controlled by diluting the antiferromagnetic CoO layer, i.e., by introducing ~i! nonmagnetic substitutions (Co12xMgxO) or ~ii! Co deficiencie (Co12yO). All intentional nonmagnetic cations or defects were placed away from the interface throughout the whole volu...
متن کاملRole of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts
The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...
متن کاملRole of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts
The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2014