Enthalpies of Formation of (Cu,Ni)3Sn, (Cu,Ni)6Sn5-HT and (Ni,Cu)3Sn2-HT
نویسندگان
چکیده
Standard enthalpies of formation of ternary phases in the Cu-Ni-Sn system were determined along sections at 25, 41 and 45.5 at.% Sn applying tin solution drop calorimetry. Generally, the interaction of Ni with Sn is much stronger than that of Cu with Sn. Along all sections the enthalpy of formation changes almost linearly with the mutual substitution of Cu and Ni within the respective homogeneity ranges. Thus no additional ternary interaction promoting the formation of further Cu-Ni-Sn phases can be assumed. The results are discussed and compared with literature values relevant to this system.
منابع مشابه
Effect of Ni on the formation of Cu6Sn5 and Cu3Sn intermetallics
In this paper, the effect of Ni on the formation of Cu6Sn5 and Cu3Sn intermetallics between tin and (Cu,Ni)-substrates has been studied by making use of the thermodynamic assessment of the Sn-Cu-Ni system. The driving forces for the diffusion of the elements in the intermetallic layers were calculated as a function of Ni-content. Assuming constant mobilities of component atoms, the results sugg...
متن کاملCross-interaction of Interfacial Reactions in Ni (au/ni/cu)-snag-cu Solder Joints during Reflow Soldering and Thermal Aging
The coupling effect of interfacial reactions between two pads in Ni-SnAg-Cu and Au/Ni/Cu-SnAg-Cu solder joints was investigated in this paper. After reflow soldering, a large amount of Cu can diffuse across the solder joint to the opposite pad to form (Cu,Ni)6Sn5 IMC on the Ni pad in Ni-SnAg-Cu solder joint. A little Ni can also be detected in Cu6Sn5 layer, which contains some trapped solder, o...
متن کاملStudy of Reactive Wetting of Sn–0.7Cu and Sn–0.3Ag–0.7Cu Lead Free Solders during Solidification on Nickel Coated Al Substrates
Microstructure, wetting behavior and interfacial reactions between Sn–0.7Cu and Sn–0.3Ag–0.7Cu (SAC0307) solders solidified on Ni coated Al substrates were compared and investigated. Microstructure of Sn–0.7Cu alloy exhibited a eutectic matrix composed of primary β-Sn dendrites with a fine dispersion of Cu6Sn5 intermetallics whereas microstructure of SAC0307 alloy exhibited coarser Cu6Sn5 and f...
متن کاملKinetics of Solid-State Reactive Diffusion in the (SnNi)/Cu System
The kinetics of the solid-state reactive diffusion between SnNi alloys and pure Cu was experimentally observed to examine effects of addition of Ni into Sn on the growth behavior of compounds at the interconnection between the Sn-base solder and the multilayer Au/Ni/Cu conductor during energization heating. In this experiment, sandwich (SnNi)/Cu/(SnNi) diffusion couples with Ni concentration...
متن کاملCombined Thermodynamic-Kinetic Analysis of the Interfacial Reactions between Ni Metallization and Various Lead-Free Solders
In this paper we will demonstrate how a thermodynamic-kinetic method can be utilized to rationalize a wide range of interfacial phenomena between Sn-based lead-free solders and Ni metallizations. First, the effect of P on the interfacial reactions, and thus on the reliability, between Sn-based solders and electroless Ni/immersion Au (ENIG) metallizations, will be discussed. Next, the effect of ...
متن کامل